Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.25 g/cm³ Show Material materials with Dichte of 1.25 g/cm³ | ISO 1183 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegemodul | 23.0 °C | 6 GPa Show Material materials with Biegemodul of 6 GPa | ISO 178 |
Dehnung | 23.0 °C | 4 % Show Material materials with Dehnung of 4 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 7 GPa Show Material materials with Elastizitätsmodul of 7 GPa | ISO 527-1/-2 |
Hardness, Ball Indentation | 23.0 °C | 200 MPa Show Material materials with Hardness, Ball Indentation of 200 MPa | ISO 2039-1 |
Poissonzahl | 23.0 °C | 0.35 [-] Show Material materials with Poissonzahl of 0.35 [-] | |
Schlagfestigkeit, Charpy gekerbt | -6.0 °C | 14 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 14 kJ/m² | ISO 179/1eA |
23.0 °C | 22 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 22 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | -6.0 °C | 80 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 80 kJ/m² | ISO 179/1eU |
23.0 °C | 80 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 80 kJ/m² | ISO 179/1eU | |
Schlagzähigkeit, Izod ungekerbt | -40.0 °C | 13 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 13 kJ/m² | ISO 180/1A |
-30.0 °C | 13 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 13 kJ/m² | ISO 180/1A | |
23.0 °C | 20 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 20 kJ/m² | ISO 180/1A | |
Zugfestigkeit | 23.0 °C | 120 MPa Show Material materials with Zugfestigkeit of 120 MPa | ISO 527-1/-2 |
Thermisch
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 258 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 258 °C | ISO 75-1/-2 | |
Heat deflection temperature, 1.80 MPa | 240 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 240 °C | ISO 75-1/-2 | |
Schmelzpunkt | 262 °C Show Material materials with Schmelzpunkt of 262 °C | ISO 11357-1/-3 | 18°F/min | |
Entflammbarkeit | Glow Wire Flammability Index, 15mil: 700 °C, Glow Wire Flammability Index, 30mil: 700 °C, Glow Wire Flammability Index, 40mil: 700 °C, Glow Wire Flammability Index, 60mil: 700 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 25% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 295°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 80°C, Min. mold temperature: 50°C, Max. mold temperature: 100°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |