Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.47 g/cm³ Show Material materials with Dichte of 1.47 g/cm³ | ISO 1183 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 300 MPa Show Material materials with Biegefestigkeit of 300 MPa | ISO 178 |
Biegemodul | 23.0 °C | 11 GPa Show Material materials with Biegemodul of 11 GPa | ISO 178 |
Dehnung | 23.0 °C | 2.4 % Show Material materials with Dehnung of 2.4 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 12.1 GPa Show Material materials with Elastizitätsmodul of 12.1 GPa | ISO 527-1/-2 |
Poissonzahl | 23.0 °C | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 10 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | ISO 179/1eA |
Schlagzähigkeit, Charpy ungekerbt | 23.0 °C | 57 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 57 kJ/m² | ISO 179/1eU |
Zugfestigkeit | 23.0 °C | 220 MPa Show Material materials with Zugfestigkeit of 220 MPa | ISO 527-1/-2 |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Glasübergangstemperatur | 135 °C Show Material materials with Glasübergangstemperatur of 135 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 1.80 MPa | 264 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 264 °C | ISO 75-1/-2 | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.8E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.8E-5 1/K | ISO 11359-1/-2 | ||
Schmelzpunkt | 300 °C Show Material materials with Schmelzpunkt of 300 °C | ISO 11357-1/-3 | first heat | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 5.7E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 5.7E-5 1/K | ISO 11359-1/-2 | ||
Entflammbarkeit | Oxygen index: 23 %, Glow Wire Flammability Index, 40mil: 750 °C, Glow Wire Ignition Temperature, 40mil: 750 °C, Glow Wire Ignition Temperature, 120mil: 800 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielektrizitätskonstante, 1 MHz | 23.0 °C | 4.3 [-] Show Material materials with Dielektrizitätskonstante, 1 MHz of 4.3 [-] | IEC 62631-2-1 |
Dielektrizitätskonstante, 100 Hz | 23.0 °C | 4.4 [-] Show Material materials with Dielektrizitätskonstante, 100 Hz of 4.4 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 100Hz of 0.02 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Durchschlagfestigkeit | 23.0 °C | 32 kV/mm Show Material materials with Durchschlagfestigkeit of 32 kV/mm | IEC 60243-1 |
Kriechstromfestigkeit | 23.0 °C | 525 V Show Material materials with Kriechstromfestigkeit of 525 V | IEC 60112 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Fillers | 35% Glass Fiber | |
| Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 6-8h, Processing Moisture Content: ≤0.1%, Melt Temperature Optimum: 325°C, Min. melt temperature: 320°C, Max. melt temperature: 330°C, Mold Temperature Optimum: 150°C, Min. mold temperature: 140°C, Max. mold temperature: 180°C | |