Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.42 g/cm³ Show Material materials with Dichte of 1.42 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 1.8 % Show Material materials with Wasserabsorption of 1.8 % | Sim. to ISO 62 | Immersion 24h |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 220 MPa Show Material materials with Biegefestigkeit of 220 MPa | ISO 178 |
Biegemodul | 23.0 °C | 9.2 GPa Show Material materials with Biegemodul of 9.2 GPa | ISO 178 |
Dehnung | 23.0 °C | 2.5 % Show Material materials with Dehnung of 2.5 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 10.2 GPa Show Material materials with Elastizitätsmodul of 10.2 GPa | ISO 527-1/-2 |
Poissonzahl | 23.0 °C | 0.34 [-] Show Material materials with Poissonzahl of 0.34 [-] | |
Schlagfestigkeit, Charpy gekerbt | -6.0 °C | 8 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 8 kJ/m² | ISO 179/1eA |
23.0 °C | 11 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 11 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | -6.0 °C | 67 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 67 kJ/m² | ISO 179/1eU |
23.0 °C | 70 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 70 kJ/m² | ISO 179/1eU | |
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 62 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 62 kJ/m² | ISO 180/1U |
23.0 °C | 63 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 63 kJ/m² | ISO 180/1U | |
Schlagzähigkeit, Izod ungekerbt | -30.0 °C | 8 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 8 kJ/m² | ISO 180/1A |
23.0 °C | 13 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 13 kJ/m² | ISO 180/1A | |
Zugfestigkeit | 23.0 °C | 145 MPa Show Material materials with Zugfestigkeit of 145 MPa | ISO 527-1/-2 |
Thermisch
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 237 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 237 °C | ISO 75-1/-2 | |
Schmelzpunkt | 248 °C Show Material materials with Schmelzpunkt of 248 °C | ISO 11357-1/-3 | 18°F/min | |
Entflammbarkeit | Burning Behav. at thickness h: HB class, Thickness tested: 1.5 mm |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 35% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 285°C, Min. melt temperature: 275°C, Max. melt temperature: 295°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 90°C, Min. mold temperature: 50°C, Max. mold temperature: 100°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm |