Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.65 g/cm³ Show Material materials with Dichte of 1.65 g/cm³ | ISO 1183 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 310 MPa Show Material materials with Biegefestigkeit of 310 MPa | ISO 178 |
Biegemodul | 23.0 °C | 17 GPa Show Material materials with Biegemodul of 17 GPa | ISO 178 |
Dehnung | 23.0 °C | 1.6 % Show Material materials with Dehnung of 1.6 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 18 GPa Show Material materials with Elastizitätsmodul of 18 GPa | ISO 527-1/-2 |
Poissonzahl | 23.0 °C | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 13 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 13 kJ/m² | ISO 179/1eA |
Schlagzähigkeit, Charpy ungekerbt | 23.0 °C | 50 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 50 kJ/m² | ISO 179/1eU |
Zugfestigkeit | 23.0 °C | 200 MPa Show Material materials with Zugfestigkeit of 200 MPa | ISO 527-1/-2 |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 215 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 215 °C | ISO 75-1/-2 | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.3E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.3E-5 1/K | ISO 11359-1/-2 | ||
Relative temperature index, electrical | 65 °C Show Material materials with Relative temperature index, electrical of 65 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 65 °C Show Material materials with Relative temperature index, mechanical impact of 65 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 65 °C Show Material materials with Relative temperature index, mechanical strength of 65 °C | UL 746B | 120mil | |||
Schmelzpunkt | 298 °C Show Material materials with Schmelzpunkt of 298 °C | ISO 11357-1/-3 | first heat | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 3.8E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 3.8E-5 1/K | ISO 11359-1/-2 | ||
Entflammbarkeit | Burning Behav. at 60mil nom. thickn.: V-0 class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: V-0 class, Thickness tested: 0.4 mm, UL recognition: yes -, FMVSS Class: DNI - | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielectric constant, 10GHz | 23.0 °C | 4.4 [-] Show Material materials with Dielectric constant, 10GHz of 4.4 [-] | ASTM D 2520 B |
Dielectric constant, 1GHz | 23.0 °C | 4.3 [-] Show Material materials with Dielectric constant, 1GHz of 4.3 [-] | ASTM D 2520 B |
Dissipation factor, 1GHz | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor, 1GHz of 0.01 [-] | ASTM D 2520 B |
Kriechstromfestigkeit | 23.0 °C | 600 V Show Material materials with Kriechstromfestigkeit of 600 V | IEC 60112 |
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Fillers | 50% Glass Fiber | |
| Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 6-8h, Processing Moisture Content: ≤0.1%, Min. melt temperature: 300°C, Max. melt temperature: 315°C, Min. mold temperature: 70°C, Max. mold temperature: 130°C | |