Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.43 g/cm³ Show Material materials with Dichte of 1.43 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 6 % Show Material materials with Wasserabsorption of 6 % | Sim. to ISO 62 | 80mil |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dehnung | 23.0 °C | 3.2 % Show Material materials with Dehnung of 3.2 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 11 GPa Show Material materials with Elastizitätsmodul of 11 GPa | ISO 527-1/-2 |
Hardness, Ball Indentation | 23.0 °C | 285 MPa Show Material materials with Hardness, Ball Indentation of 285 MPa | ISO 2039-1 |
Hardness, Rockwell R | 23.0 °C | 125 [-] Show Material materials with Hardness, Rockwell R of 125 [-] | ISO 2039-2 |
Härte, Rockwell M | 23.0 °C | 110 [-] Show Material materials with Härte, Rockwell M of 110 [-] | ISO 2039-2 |
Poissonzahl | 23.0 °C | 0.34 [-] Show Material materials with Poissonzahl of 0.34 [-] | |
Schlagfestigkeit, Charpy gekerbt | -40.0 °C | 12 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 12 kJ/m² | ISO 179/1eA |
23.0 °C | 12 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 12 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | -6.0 °C | 70 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 70 kJ/m² | ISO 179/1eU |
23.0 °C | 75 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 75 kJ/m² | ISO 179/1eU | |
Zugfestigkeit | 23.0 °C | 200 MPa Show Material materials with Zugfestigkeit of 200 MPa | ISO 527-1/-2 |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Glasübergangstemperatur | 85 °C Show Material materials with Glasübergangstemperatur of 85 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 0.45 MPa | 261 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 261 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 242 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 242 °C | ISO 75-1/-2 | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.8E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.8E-5 1/K | ISO 11359-1/-2 | ||
Schmelzpunkt | 267 °C Show Material materials with Schmelzpunkt of 267 °C | ISO 11357-1/-3 | 18°F/min | |||
Spezifische Wärmekapazität | 23.0 °C | 2300 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 2300 J/(kg·K) | of melt | ||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 7.2E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 7.2E-5 1/K | ISO 11359-1/-2 | ||
Entflammbarkeit | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, FMVSS Class: B -, Burning rate, Thickness 1 mm: 44 mm/min |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Durchschlagfestigkeit | 23.0 °C | 20 kV/mm Show Material materials with Durchschlagfestigkeit of 20 kV/mm | IEC 60243-1 | Short Time, 2mm |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 35% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 285°C, Min. melt temperature: 280°C, Max. melt temperature: 290°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |