Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.36 g/cm³ Show Material materials with Dichte of 1.36 g/cm³ | ISO 1183 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dehnung | 23.0 °C | 3.1 % Show Material materials with Dehnung of 3.1 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 7.5 GPa Show Material materials with Elastizitätsmodul of 7.5 GPa | ISO 527-1/-2 |
Hardness, Ball Indentation | 23.0 °C | 235 MPa Show Material materials with Hardness, Ball Indentation of 235 MPa | ISO 2039-1 |
Poissonzahl | 23.0 °C | 0.34 [-] Show Material materials with Poissonzahl of 0.34 [-] | |
Zugfestigkeit | 23.0 °C | 140 MPa Show Material materials with Zugfestigkeit of 140 MPa | ISO 527-1/-2 |
Thermisch
Property | Value | Comment | |
---|---|---|---|
Schmelzpunkt | 259 °C Show Material materials with Schmelzpunkt of 259 °C | ISO 11357-1/-3 | 18°F/min | |
Entflammbarkeit | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Technological properties
Property | ||
---|---|---|
Fillers | 30% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 290°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |