Zytel® HTNFE8200 BK431

Want to keep this datasheet? Save it now in your required format

Description

Zytel® HTN high performance polyamide resins feature high retention of properties upon exposure to elevated temperature, to high moisture, and to harsh chemical environments. Polymer families and grades of Zytel® HTN are tailored to optimize performance as well as processability. Typical applications with Zytel® HTN include demanding applications in the automotive, electrical and electronics, domestic appliances, and construction industries. Zytel® HTNFE8200 BK431 is an unreinforced, toughened, heat stabilized high performance polyamide resin for injection molding. It is also a PPA resin.

Equivalent Materials

ISO 16396-PA6T

Diese Materialdaten wurden von Matmatch zur Verfügung gestellt

Alle Daten beziehen sich auf Raumtemperatur soweit nicht anderweitig spezifiziert. SI Einheiten werden verwendt soweit nicht anderweitig spezifiziert.
Äquivalente Standards sind ähnlich zu einem oder mehreren Standards die der Anbieter angegeben hat. Manche äquivalente Standards können strikter sein oder außerhalb der Bedingungen des ursprünglichen Standards.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Eigenschaften

Allgemein

Property	Temperature	Value	Comment
Dichte	23.0 °C	1.13 g/cm³ Show Material materials with Dichte of 1.13 g/cm³	ISO 1183

Mechanisch

Property	Temperature	Value	Comment
Biegemodul	23.0 °C	2.1 GPa Show Material materials with Biegemodul of 2.1 GPa	ISO 178
Dehnung	23.0 °C	14 % Show Material materials with Dehnung of 14 %	ISO 527-1/-2
Elastizitätsmodul	23.0 °C	2.2 GPa Show Material materials with Elastizitätsmodul of 2.2 GPa	ISO 527-1/-2
Elongation at yield	23.0 °C	5.5 % Show Material materials with Elongation at yield of 5.5 %	ISO 527-1/-2
Poissonzahl	23.0 °C	0.39 [-] Show Material materials with Poissonzahl of 0.39 [-]
Schlagfestigkeit, Charpy gekerbt	23.0 °C	80 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 80 kJ/m²	ISO 179/1eA
Streckgrenze	23.0 °C	69 MPa Show Material materials with Streckgrenze of 69 MPa	ISO 527-1/-2
Schlagzähigkeit, Charpy ungekerbt	No Break @ 23,-6°C, ISO 179/1eA

Thermisch

Property	Value	Comment
Heat deflection temperature, 0.45 MPa	138 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 138 °C	ISO 75-1/-2
Heat deflection temperature, 1.80 MPa	125 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 125 °C	ISO 75-1/-2
Schmelzpunkt	300 °C Show Material materials with Schmelzpunkt of 300 °C	ISO 11357-1/-3 \| first heat
Entflammbarkeit	FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min

Elektrisch

Property	Temperature	Value	Comment
Volume resistivity	23.0 °C	1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm	min. \| IEC 62631-3-1

Rheological Properties

Property	Temperature	Value	Comment
Schrumpfung	23.0 °C	1 % Show Material materials with Schrumpfung of 1 %	ISO 294-4, 2577
Schrumpfung, diagonal	23.0 °C	1 % Show Material materials with Schrumpfung, diagonal of 1 %	ISO 294-4, 2577

Technological properties

Property
Processing methods	Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 6-8h, Processing Moisture Content: ≤0.1%, Melt Temperature Optimum: 325°C, Min. melt temperature: 320°C, Max. melt temperature: 330°C, Min. mold temperature: 80°C, Max. mold temperature: 120°C