| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.05 g/cm³ Show Material materials with Dichte of 1.05 g/cm³ | ISO 1183 |
Mechanisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Biegemodul | 23.0 °C | 0.9 GPa Show Material materials with Biegemodul of 0.9 GPa | ISO 178 | ||
Dehnung | 23.0 °C | 500 % Show Material materials with Dehnung of 500 % | min. | ISO 527-1/-2 | ||
Elastizitätsmodul | 23.0 °C | 1.15 GPa Show Material materials with Elastizitätsmodul of 1.15 GPa | ISO 527-1/-2 | ||
Elongation at yield | 23.0 °C | 19 % Show Material materials with Elongation at yield of 19 % | ISO 527-1/-2 | ||
Poissonzahl | 23.0 °C | 0.44 [-] Show Material materials with Poissonzahl of 0.44 [-] | |||
Schlagfestigkeit, Charpy gekerbt | -6.0 °C | 11 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 11 kJ/m² | ISO 179/1eA | ||
23.0 °C | 65 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 65 kJ/m² | ISO 179/1eA | |||
Streckgrenze | 23.0 °C | 37.2 MPa Show Material materials with Streckgrenze of 37.2 MPa | ISO 527-1/-2 | ||
Zugfestigkeit | 23.0 °C | 36 MPa Show Material materials with Zugfestigkeit of 36 MPa | ISO 527-1/-2 | 50mm/min | ||
Schlagzähigkeit, Charpy ungekerbt | No Break @ 23°C,ISO 179/1eU | ||||
Thermisch
| Property | Value | Comment | |
|---|---|---|---|
Glasübergangstemperatur | 40 °C Show Material materials with Glasübergangstemperatur of 40 °C | ISO 11357-1/-2 | 18°F/min | |
Heat deflection temperature, 1.80 MPa | 43 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 43 °C | ISO 75-1/-2 | |
Schmelzpunkt | 220 °C Show Material materials with Schmelzpunkt of 220 °C | ISO 11357-1/-3 | 18°F/min | |
Entflammbarkeit | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min | ||
Technological properties