| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.14 g/cm³ Show Material materials with Dichte of 1.14 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 8.5 % Show Material materials with Wasserabsorption of 8.5 % | Sim. to ISO 62 | 80mil |
Mechanisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Dehnung | 23.0 °C | 500 % Show Material materials with Dehnung of 500 % | min. | ISO 527-1/-2 | ||
Elastizitätsmodul | 23.0 °C | 3.1 GPa Show Material materials with Elastizitätsmodul of 3.1 GPa | ISO 527-1/-2 | ||
Elongation at yield | 23.0 °C | 5 % Show Material materials with Elongation at yield of 5 % | ISO 527-1/-2 | ||
Poissonzahl | 23.0 °C | 0.37 [-] Show Material materials with Poissonzahl of 0.37 [-] | |||
Schlagfestigkeit, Charpy gekerbt | -6.0 °C | 5 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 5 kJ/m² | ISO 179/1eA | ||
23.0 °C | 6 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 6 kJ/m² | ISO 179/1eA | |||
Schlagzähigkeit, Izod ungekerbt | -30.0 °C | 4.3 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 4.3 kJ/m² | ISO 180/1A | ||
23.0 °C | 5.5 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 5.5 kJ/m² | ISO 180/1A | |||
Streckgrenze | 23.0 °C | 86 MPa Show Material materials with Streckgrenze of 86 MPa | ISO 527-1/-2 | ||
Schlagzähigkeit, Charpy ungekerbt | No Break @ 23,-6°C, ISO 179/1eA | ||||
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Glasübergangstemperatur | 70 °C Show Material materials with Glasübergangstemperatur of 70 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 0.45 MPa | 205 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 205 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 72 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 72 °C | ISO 75-1/-2 | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1E-4 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1E-4 1/K | ISO 11359-1/-2 | ||
Schmelzpunkt | 263 °C Show Material materials with Schmelzpunkt of 263 °C | ISO 11357-1/-3 | 18°F/min | |||
Spezifische Wärmekapazität | 23.0 °C | 2790 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 2790 J/(kg·K) | of melt | ||
Vicat-Erweichungstemperatur | 244 °C Show Material materials with Vicat-Erweichungstemperatur of 244 °C | ISO 306 | 90°F/h, 11 lbf | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1E-4 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 1E-4 1/K | ISO 11359-1/-2 | ||
Entflammbarkeit | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.81 mm, UL recognition: yes -, Oxygen index: 28 %, Glow Wire Flammability Index, 15mil: 960 °C, Glow Wire Flammability Index, 30mil: 960 °C, Glow Wire Flammability Index, 40mil: 960 °C, Glow Wire Flammability Index, 60mil: 960 °C, Glow Wire Flammability Index, 80mil: 960 °C, Glow Wire Flammability Index, 120mil: 960 °C, Glow Wire Ignition Temperature, 30mil: 930 °C, Glow Wire Ignition Temperature, 15mil: 930 °C, Glow Wire Ignition Temperature, 80mil: 800 °C, Glow Wire Ignition Temperature, 120mil: 725 °C, Glow Wire Temperature, No Flame, 40mil: 750 °C, Glow Wire Temperature, No Flame, 80mil: 725 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielektrizitätskonstante, 1 MHz | 23.0 °C | 3.6 [-] Show Material materials with Dielektrizitätskonstante, 1 MHz of 3.6 [-] | IEC 62631-2-1 |
Dielektrizitätskonstante, 100 Hz | 23.0 °C | 4.3 [-] Show Material materials with Dielektrizitätskonstante, 100 Hz of 4.3 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 100Hz of 0.02 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Durchschlagfestigkeit | 23.0 °C | 30.5 kV/mm Show Material materials with Durchschlagfestigkeit of 30.5 kV/mm | IEC 60243-1 |
Volume resistivity | 23.0 °C | 1.00E+13 Ω·cm Show Material materials with Volume resistivity of 1.00E+13 Ω·cm | IEC 62631-3-1 |
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.05%, Melt Temperature Optimum: 290°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Max. screw tangential speed: 0.4m/s, Mold Temperature Optimum: 70°C, Min. mold temperature: 50°C, Max. mold temperature: 90°C, Hold pressure range: 50-100MPa, Hold pressure time: 4s/mm, Ejection temperature: 190°C | |