Allgemein
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dehnung | 23.0 °C | 5 % Show Material materials with Dehnung of 5 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 5 GPa Show Material materials with Elastizitätsmodul of 5 GPa | ISO 527-1/-2 |
Hardness, Ball Indentation | 23.0 °C | 180 MPa Show Material materials with Hardness, Ball Indentation of 180 MPa | ISO 2039-1 |
Poissonzahl | 23.0 °C | 0.35 [-] Show Material materials with Poissonzahl of 0.35 [-] | |
Schlagfestigkeit, Charpy gekerbt | -40.0 °C | 12 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 12 kJ/m² | ISO 179/1eA |
-6.0 °C | 13 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 13 kJ/m² | ISO 179/1eA | |
23.0 °C | 21 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 21 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | 23.0 °C | 80 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 80 kJ/m² | ISO 179/1eU |
Schlagzähigkeit, Izod ungekerbt | -30.0 °C | 11 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 11 kJ/m² | ISO 180/1A |
23.0 °C | 21 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 21 kJ/m² | ISO 180/1A | |
Zugfestigkeit | 23.0 °C | 100 MPa Show Material materials with Zugfestigkeit of 100 MPa | ISO 527-1/-2 |
Thermisch
Property | Value | Comment | |
---|---|---|---|
Glasübergangstemperatur | 60 °C Show Material materials with Glasübergangstemperatur of 60 °C | ISO 11357-1/-2 | 18°F/min | |
Heat deflection temperature, 0.45 MPa | 215 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 215 °C | ISO 75-1/-2 | |
Heat deflection temperature, 1.80 MPa | 190 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 190 °C | ISO 75-1/-2 | |
Schmelzpunkt | 221 °C Show Material materials with Schmelzpunkt of 221 °C | ISO 11357-1/-3 | 18°F/min | |
Entflammbarkeit | Oxygen index: 25 %, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dissipation factor, 100Hz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 100Hz of 0.02 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Kriechstromfestigkeit | 23.0 °C | 600 V Show Material materials with Kriechstromfestigkeit of 600 V | IEC 60112 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | IEC 62631-3-1 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt viscosity | 280.0 °C | 300 Pa·s Show Material materials with Melt viscosity of 300 Pa·s | ISO 11443 | @ 1000 sec-1, 280°C |
Schrumpfung | 23.0 °C | 0.7 % Show Material materials with Schrumpfung of 0.7 % | ISO 294-4, 2577 |
Schrumpfung, diagonal | 23.0 °C | 1.2 % Show Material materials with Schrumpfung, diagonal of 1.2 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Fillers | 15% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 270°C, Min. melt temperature: 260°C, Max. melt temperature: 280°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm |