Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.04 g/cm³ Show Material materials with Dichte of 1.04 g/cm³ | ISO 1183 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegemodul | 23.0 °C | 0.9 GPa Show Material materials with Biegemodul of 0.9 GPa | ISO 178 |
Dehnung | 23.0 °C | 500 % Show Material materials with Dehnung of 500 % | min. | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 0.9 GPa Show Material materials with Elastizitätsmodul of 0.9 GPa | ISO 527-1/-2 |
Poissonzahl | 23.0 °C | 0.45 [-] Show Material materials with Poissonzahl of 0.45 [-] | |
Schlagfestigkeit, Charpy gekerbt | -40.0 °C | 30 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 30 kJ/m² | ISO 179/1eA |
23.0 °C | 105 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 105 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Izod ungekerbt | -40.0 °C | 25 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 25 kJ/m² | ISO 180/1A |
23.0 °C | 95 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 95 kJ/m² | ISO 180/1A | |
Thermisch
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 68 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 68 °C | ISO 75-1/-2 | |
Heat deflection temperature, 1.80 MPa | 50 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 50 °C | ISO 75-1/-2 | |
Schmelzpunkt | 263 °C Show Material materials with Schmelzpunkt of 263 °C | ISO 11357-1/-3 | 18°F/min | |
Entflammbarkeit | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 285°C, Min. melt temperature: 275°C, Max. melt temperature: 295°C, Mold Temperature Optimum: 60°C, Min. mold temperature: 40°C, Max. mold temperature: 80°C |