Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.47 g/cm³ Show Material materials with Dichte of 1.47 g/cm³ | ISO 1183 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 210 MPa Show Material materials with Biegefestigkeit of 210 MPa | ISO 178 |
Biegemodul | 23.0 °C | 11 GPa Show Material materials with Biegemodul of 11 GPa | ISO 178 |
Dehnung | 23.0 °C | 1.7 % Show Material materials with Dehnung of 1.7 % | ISO 527-1/-2 |
Schlagfestigkeit, Charpy gekerbt | -6.0 °C | 6 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 6 kJ/m² | ISO 179/1eA |
23.0 °C | 7 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 7 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | -6.0 °C | 35 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 35 kJ/m² | ISO 179/1eU |
23.0 °C | 35 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 35 kJ/m² | ISO 179/1eU | |
Zugfestigkeit | 23.0 °C | 130 MPa Show Material materials with Zugfestigkeit of 130 MPa | ISO 527-1/-2 |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Glasübergangstemperatur | 80 °C Show Material materials with Glasübergangstemperatur of 80 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 1.80 MPa | 277 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 277 °C | ISO 75-1/-2 | annealed | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 2E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2E-5 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Relative temperature index, electrical | 130 °C Show Material materials with Relative temperature index, electrical of 130 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 120 °C Show Material materials with Relative temperature index, mechanical impact of 120 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 130 °C Show Material materials with Relative temperature index, mechanical strength of 130 °C | UL 746B | 120mil | |||
Schmelzpunkt | 314 °C Show Material materials with Schmelzpunkt of 314 °C | ISO 11357-1/-3 | first heat | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 8.4E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 8.4E-5 1/K | ISO 11359-1/-2 | 55 - 160°C | ||
Entflammbarkeit | Burning Behav. at thickness h: V-0 class, Thickness tested: 0.4 mm, UL recognition: yes -, Glow Wire Flammability Index, 15mil: 960 °C, Glow Wire Flammability Index, 60mil: 960 °C, Glow Wire Flammability Index, 120mil: 960 °C, Glow Wire Ignition Temperature, 15mil: 750 °C, Glow Wire Ignition Temperature, 60mil: 800 °C, Glow Wire Ignition Temperature, 120mil: 825 °C, Railway classification: R23 -, Railway classification rating: HL1 - | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielectric constant, 10GHz | 23.0 °C | 3.8 [-] Show Material materials with Dielectric constant, 10GHz of 3.8 [-] | ASTM D 2520 B |
Dielectric constant, 1GHz | 23.0 °C | 3.7 [-] Show Material materials with Dielectric constant, 1GHz of 3.7 [-] | ASTM D 2520 B |
Dissipation factor, 1GHz | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor, 1GHz of 0.01 [-] | ASTM D 2520 B |
Durchschlagfestigkeit | 23.0 °C | 33 kV/mm Show Material materials with Durchschlagfestigkeit of 33 kV/mm | IEC 60243-1 |
Kriechstromfestigkeit | 23.0 °C | 600 V Show Material materials with Kriechstromfestigkeit of 600 V | IEC 60112 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Fillers | 30% Glass Fiber | |
| Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 6-8h, Processing Moisture Content: ≤0.1%, Min. melt temperature: 330°C, Max. melt temperature: 335°C, Min. mold temperature: 110°C, Max. mold temperature: 130°C | |