Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.14 g/cm³ Show Material materials with Dichte of 1.14 g/cm³ | ISO 1183 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dehnung | 23.0 °C | 14 % Show Material materials with Dehnung of 14 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 3.8 GPa Show Material materials with Elastizitätsmodul of 3.8 GPa | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 6 % Show Material materials with Elongation at yield of 6 % | ISO 527-1/-2 |
Poissonzahl | 23.0 °C | 0.36 [-] Show Material materials with Poissonzahl of 0.36 [-] | |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 3 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 3 kJ/m² | ISO 179/1eA |
Streckgrenze | 23.0 °C | 94 MPa Show Material materials with Streckgrenze of 94 MPa | ISO 527-1/-2 |
Thermisch
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 78 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 78 °C | ISO 75-1/-2 | |
Schmelzpunkt | 262 °C Show Material materials with Schmelzpunkt of 262 °C | ISO 11357-1/-3 | 18°F/min | |
Entflammbarkeit | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 290°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Max. screw tangential speed: 0.4m/s, Mold Temperature Optimum: 70°C, Min. mold temperature: 50°C, Max. mold temperature: 90°C, Hold pressure range: 50-100MPa, Hold pressure time: 4s/mm, Ejection temperature: 190°C |