Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.25 g/cm³ Show Material materials with Dichte of 1.25 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 5.2 % Show Material materials with Wasserabsorption of 5.2 % | Sim. to ISO 62 | 80mil |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 160 MPa Show Material materials with Biegefestigkeit of 160 MPa | ISO 178 |
Biegemodul | 23.0 °C | 6 GPa Show Material materials with Biegemodul of 6 GPa | ISO 178 |
Dehnung | 23.0 °C | 4 % Show Material materials with Dehnung of 4 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 6.5 GPa Show Material materials with Elastizitätsmodul of 6.5 GPa | ISO 527-1/-2 |
Hardness, Ball Indentation | 23.0 °C | 225 MPa Show Material materials with Hardness, Ball Indentation of 225 MPa | ISO 2039-1 |
Poissonzahl | 23.0 °C | 0.35 [-] Show Material materials with Poissonzahl of 0.35 [-] | |
Schlagfestigkeit, Charpy gekerbt | -40.0 °C | 7.5 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 7.5 kJ/m² | ISO 179/1eA |
-6.0 °C | 8 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 8 kJ/m² | ISO 179/1eA | |
23.0 °C | 15 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 15 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | -6.0 °C | 40 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 40 kJ/m² | ISO 179/1eU |
23.0 °C | 80 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 80 kJ/m² | ISO 179/1eU | |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 73 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 73 kJ/m² | ISO 180/1U |
Schlagzähigkeit, Izod ungekerbt | -30.0 °C | 8 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 8 kJ/m² | ISO 180/1A |
23.0 °C | 14 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 14 kJ/m² | ISO 180/1A | |
Schubmodule | 23.0 °C | 1.4 GPa Show Material materials with Schubmodule of 1.4 GPa | ISO 6721 |
Zugfestigkeit | 23.0 °C | 120 MPa Show Material materials with Zugfestigkeit of 120 MPa | ISO 527-1/-2 |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Glasübergangstemperatur | 60 °C Show Material materials with Glasübergangstemperatur of 60 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 0.45 MPa | 257 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 257 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 239 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 239 °C | ISO 75-1/-2 | |||
Schmelzpunkt | 260 °C Show Material materials with Schmelzpunkt of 260 °C | ISO 11357-1/-3 | 18°F/min | |||
Spezifische Wärmekapazität | 23.0 °C | 2000 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 2000 J/(kg·K) | of melt | ||
Entflammbarkeit | FMVSS Class: SE |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt viscosity | 280.0 °C | 330 Pa·s Show Material materials with Melt viscosity of 330 Pa·s | ISO 11443 | @ 1000 sec-1, 280°C |
Schrumpfung | 23.0 °C | 0.5 % Show Material materials with Schrumpfung of 0.5 % | ISO 294-4, 2577 |
Schrumpfung, diagonal | 23.0 °C | 0.7 % Show Material materials with Schrumpfung, diagonal of 0.7 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Fillers | 20% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 295°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 90°C, Min. mold temperature: 50°C, Max. mold temperature: 100°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |