Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.09 g/cm³ Show Material materials with Dichte of 1.09 g/cm³ | ISO 1183 |
Mechanisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Dehnung | 23.0 °C | 500 % Show Material materials with Dehnung of 500 % | min. | ISO 527-1/-2 | ||
Elastizitätsmodul | 23.0 °C | 2.2 GPa Show Material materials with Elastizitätsmodul of 2.2 GPa | ISO 527-1/-2 | ||
Elongation at yield | 23.0 °C | 4.2 % Show Material materials with Elongation at yield of 4.2 % | ISO 527-1/-2 | ||
Poissonzahl | 23.0 °C | 0.39 [-] Show Material materials with Poissonzahl of 0.39 [-] | |||
Schlagfestigkeit, Charpy gekerbt | -40.0 °C | 15 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 15 kJ/m² | ISO 179/1eA | ||
-6.0 °C | 22 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 22 kJ/m² | ISO 179/1eA | |||
23.0 °C | 45 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 45 kJ/m² | ISO 179/1eA | |||
Schlagzähigkeit, Izod ungekerbt | -30.0 °C | 18 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 18 kJ/m² | ISO 180/1A | ||
23.0 °C | 38 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 38 kJ/m² | ISO 180/1A | |||
Streckgrenze | 23.0 °C | 60 MPa Show Material materials with Streckgrenze of 60 MPa | ISO 527-1/-2 | ||
Schlagzähigkeit, Charpy ungekerbt | No Break @ 23,-6°C, ISO 179/1eA |
Thermisch
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 100 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 100 °C | ISO 75-1/-2 | |
Heat deflection temperature, 1.80 MPa | 52 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 52 °C | ISO 75-1/-2 | |
Schmelzpunkt | 220 °C Show Material materials with Schmelzpunkt of 220 °C | ISO 11357-1/-3 | 18°F/min | |
Entflammbarkeit | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt viscosity | 280.0 °C | 440 Pa·s Show Material materials with Melt viscosity of 440 Pa·s | ISO 11443 | @ 1000 sec-1, 280°C |
Schrumpfung | 23.0 °C | 1.1 % Show Material materials with Schrumpfung of 1.1 % | ISO 294-4, 2577 |
Schrumpfung, diagonal | 23.0 °C | 1.1 % Show Material materials with Schrumpfung, diagonal of 1.1 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 270°C, Min. melt temperature: 260°C, Max. melt temperature: 280°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 70°C, Min. mold temperature: 50°C, Max. mold temperature: 100°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm |