Zytel® FE4200 BK136

Alternative und Handelsbezeichungen
PA66-HI

Want to keep this datasheet? Save it now in your required format

Description

Common features of Zytel® nylon resin include mechanical and physical properties such as high mechanical strength, excellent balance of stiffness and toughness, good high temperature performance, good electrical and flammability properties, good abrasion and chemical resistance. In addition, Zytel® nylon resins are available in different modified and reinforced grades to create a wide range of products with tailored properties for specific processes and end-uses. Zytel® nylon resin, including most flame retardant grades, offer the ability to be coloured. The good melt stability of Zytel® nylon resin normally enables the recycling of properly handled production waste. If recycling is not possible, DuPont recommends, as the preferred option, incineration with energy recovery (-31kJ/g of base polymer) in appropriately equipped installations. For disposal, local regulations have to be observed.Zytel® nylon resin typically is used in demanding applications in the automotive, furniture, domestic appliances, sporting goods and construction industry.Zytel® FE4200 BK136 is a low die deposit polyamide 66 extrusion resin.

Equivalent Materials

Diese Materialdaten wurden von Matmatch zur Verfügung gestellt

Alle Daten beziehen sich auf Raumtemperatur soweit nicht anderweitig spezifiziert. SI Einheiten werden verwendt soweit nicht anderweitig spezifiziert.
Äquivalente Standards sind ähnlich zu einem oder mehreren Standards die der Anbieter angegeben hat. Manche äquivalente Standards können strikter sein oder außerhalb der Bedingungen des ursprünglichen Standards.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Eigenschaften

Allgemein

Property	Temperature	Value	Comment
Dichte	23.0 °C	1.06 g/cm³ Show Material materials with Dichte of 1.06 g/cm³	ISO 1183

Mechanisch

Property	Temperature	Value	Comment
Biegemodul	23.0 °C	1.79 GPa Show Material materials with Biegemodul of 1.79 GPa	ISO 178
Elastizitätsmodul	23.0 °C	1.9 GPa Show Material materials with Elastizitätsmodul of 1.9 GPa	ISO 527-1/-2
Elongation at yield	23.0 °C	4.9 % Show Material materials with Elongation at yield of 4.9 %	ISO 527-1/-2
Poissonzahl	23.0 °C	0.41 [-] Show Material materials with Poissonzahl of 0.41 [-]
Schlagfestigkeit, Charpy gekerbt	23.0 °C	74 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 74 kJ/m²	ISO 179/1eA
Streckgrenze	23.0 °C	49 MPa Show Material materials with Streckgrenze of 49 MPa	ISO 527-1/-2

Thermisch

Property	Value	Comment
Heat deflection temperature, 0.45 MPa	98 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 98 °C	ISO 75-1/-2
Heat deflection temperature, 1.80 MPa	62 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 62 °C	ISO 75-1/-2
Schmelzpunkt	261 °C Show Material materials with Schmelzpunkt of 261 °C	ISO 11357-1/-3 \| 18°F/min
Entflammbarkeit	FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min

Rheological Properties

Property	Temperature	Value	Comment
Schrumpfung	23.0 °C	1.7 % Show Material materials with Schrumpfung of 1.7 %	ISO 294-4, 2577
Schrumpfung, diagonal	23.0 °C	1 % Show Material materials with Schrumpfung, diagonal of 1 %	ISO 294-4, 2577

Technological properties

Property
Processing methods	Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 290°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Max. screw tangential speed: 0.3m/s, Mold Temperature Optimum: 80°C, Min. mold temperature: 50°C, Max. mold temperature: 100°C, Hold pressure range: 50-100MPa, Hold pressure time: 4s/mm, Ejection temperature: 190°C

Zytel® FE4200 BK136

Description

Equivalent Materials

Ashby charts

Empfohlene Literatur

Eigenschaften