| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.25 g/cm³ Show Material materials with Dichte of 1.25 g/cm³ | ISO 1183 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 210 MPa Show Material materials with Biegefestigkeit of 210 MPa | ISO 178 |
Biegemodul | 23.0 °C | 4.9 GPa Show Material materials with Biegemodul of 4.9 GPa | ISO 178 |
Dehnung | 23.0 °C | 3.5 % Show Material materials with Dehnung of 3.5 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 5.5 GPa Show Material materials with Elastizitätsmodul of 5.5 GPa | ISO 527-1/-2 |
Poissonzahl | 23.0 °C | 0.35 [-] Show Material materials with Poissonzahl of 0.35 [-] | |
Schlagfestigkeit, Charpy gekerbt | -40.0 °C | 5 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 5 kJ/m² | ISO 179/1eA |
23.0 °C | 6 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 6 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | 23.0 °C | 60 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 60 kJ/m² | ISO 179/1eU |
Zugfestigkeit | 23.0 °C | 130 MPa Show Material materials with Zugfestigkeit of 130 MPa | ISO 527-1/-2 |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 277 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 277 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 230 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 230 °C | ISO 75-1/-2 | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 3.4E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 3.4E-5 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Relative temperature index, electrical | 150 °C Show Material materials with Relative temperature index, electrical of 150 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 130 °C Show Material materials with Relative temperature index, mechanical impact of 130 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 140 °C Show Material materials with Relative temperature index, mechanical strength of 140 °C | UL 746B | 120mil | |||
Schmelzpunkt | 300 °C Show Material materials with Schmelzpunkt of 300 °C | ISO 11357-1/-3 | first heat | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 7E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 7E-5 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Entflammbarkeit | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.8 mm, UL recognition: yes -, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | IEC 62631-3-1 |
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Fillers | 15% Glass Fiber | |
| Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 6-8h, Processing Moisture Content: ≤0.1%, Melt Temperature Optimum: 325°C, Min. melt temperature: 320°C, Max. melt temperature: 330°C, Min. mold temperature: 90°C, Max. mold temperature: 110°C | |