Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.41 g/cm³ Show Material materials with Dichte of 1.41 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 5.4 % Show Material materials with Wasserabsorption of 5.4 % | Sim. to ISO 62 | 80mil |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dehnung | 23.0 °C | 3.5 % Show Material materials with Dehnung of 3.5 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 12 GPa Show Material materials with Elastizitätsmodul of 12 GPa | ISO 527-1/-2 |
Poissonzahl | 23.0 °C | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | |
Schlagfestigkeit, Charpy gekerbt | -6.0 °C | 17 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 17 kJ/m² | ISO 179/1eA |
23.0 °C | 24 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 24 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | -6.0 °C | 118 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 118 kJ/m² | ISO 179/1eU |
23.0 °C | 110 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 110 kJ/m² | ISO 179/1eU | |
Schlagzähigkeit, Izod ungekerbt | -30.0 °C | 19 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 19 kJ/m² | ISO 180/1A |
23.0 °C | 24 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 24 kJ/m² | ISO 180/1A | |
Zugfestigkeit | 23.0 °C | 190 MPa Show Material materials with Zugfestigkeit of 190 MPa | ISO 527-1/-2 |
Thermisch
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 212 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 212 °C | ISO 75-1/-2 | |
Schmelzpunkt | 221 °C Show Material materials with Schmelzpunkt of 221 °C | ISO 11357-1/-3 | 18°F/min | |
Entflammbarkeit | FMVSS Class: B -, Burning rate, Thickness 1 mm: 33 mm/min |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 40% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 270°C, Min. melt temperature: 260°C, Max. melt temperature: 280°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 50°C, Max. mold temperature: 90°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm |