Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.06 g/cm³ Show Material materials with Dichte of 1.06 g/cm³ | ISO 1183 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dehnung | 23.0 °C | 50 % Show Material materials with Dehnung of 50 % | ISO 527-1/-2 | 50mm/min |
Elastizitätsmodul | 23.0 °C | 2.4 GPa Show Material materials with Elastizitätsmodul of 2.4 GPa | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 4.3 % Show Material materials with Elongation at yield of 4.3 % | ISO 527-1/-2 |
Poissonzahl | 23.0 °C | 0.38 [-] Show Material materials with Poissonzahl of 0.38 [-] | |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 5 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 5 kJ/m² | ISO 179/1eA |
Streckgrenze | 23.0 °C | 65 MPa Show Material materials with Streckgrenze of 65 MPa | ISO 527-1/-2 |
Zugfestigkeit | 23.0 °C | 40 MPa Show Material materials with Zugfestigkeit of 40 MPa | ISO 527-1/-2 | 50mm/min |
Thermisch
| Property | Value | Comment | |
|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 150 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 150 °C | ISO 75-1/-2 | |
Schmelzpunkt | 216 °C Show Material materials with Schmelzpunkt of 216 °C | ISO 11357-1/-3 | 18°F/min | |
Entflammbarkeit | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min | ||
Technological properties
| Property | ||
|---|---|---|
| Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.15%, Min. melt temperature: 230°C, Max. melt temperature: 290°C, Min. mold temperature: 50°C, Max. mold temperature: 90°C | |