Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.07 g/cm³ Show Material materials with Dichte of 1.07 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 3.3 % Show Material materials with Wasserabsorption of 3.3 % | Sim. to ISO 62 | 80mil |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegemodul | 23.0 °C | 1.9 GPa Show Material materials with Biegemodul of 1.9 GPa | ISO 178 |
Dehnung | 23.0 °C | 230 % Show Material materials with Dehnung of 230 % | ISO 527-1/-2 | 50mm/min |
Elastizitätsmodul | 23.0 °C | 2 GPa Show Material materials with Elastizitätsmodul of 2 GPa | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 5 % Show Material materials with Elongation at yield of 5 % | ISO 527-1/-2 |
Härte, Rockwell M | 23.0 °C | 75 [-] Show Material materials with Härte, Rockwell M of 75 [-] | ISO 2039-2 |
Poissonzahl | 23.0 °C | 0.4 [-] Show Material materials with Poissonzahl of 0.4 [-] | |
Schlagfestigkeit, Charpy gekerbt | -40.0 °C | 7 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 7 kJ/m² | ISO 179/1eA |
23.0 °C | 8 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 8 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 5 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 5 kJ/m² | ISO 180/1A |
Streckgrenze | 23.0 °C | 64 MPa Show Material materials with Streckgrenze of 64 MPa | ISO 527-1/-2 |
Zugfestigkeit | 23.0 °C | 62 MPa Show Material materials with Zugfestigkeit of 62 MPa | ISO 527-1/-2 | 50mm/min |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Glasübergangstemperatur | 60 °C Show Material materials with Glasübergangstemperatur of 60 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 0.45 MPa | 155 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 155 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 55 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 55 °C | ISO 75-1/-2 | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 9E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 9E-5 1/K | ISO 11359-1/-2 | ||
Schmelzpunkt | 223 °C Show Material materials with Schmelzpunkt of 223 °C | ISO 11357-1/-3 | 18°F/min | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1.5E-4 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.5E-4 1/K | ISO 11359-1/-2 | ||
Entflammbarkeit | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, Burning Behav. at thickness h: HB class, Thickness tested: 3 mm, Oxygen index: 24 %, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielectric constant, 10GHz | 23.0 °C | 2.7 [-] Show Material materials with Dielectric constant, 10GHz of 2.7 [-] | ASTM D 2520 B |
Dielectric constant, 1GHz | 23.0 °C | 2.8 [-] Show Material materials with Dielectric constant, 1GHz of 2.8 [-] | ASTM D 2520 B |
Dielektrizitätskonstante, 1 MHz | 23.0 °C | 3.3 [-] Show Material materials with Dielektrizitätskonstante, 1 MHz of 3.3 [-] | IEC 62631-2-1 |
Dielektrizitätskonstante, 100 Hz | 23.0 °C | 3.9 [-] Show Material materials with Dielektrizitätskonstante, 100 Hz of 3.9 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 0.04 [-] Show Material materials with Dissipation factor, 100Hz of 0.04 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.03 [-] Show Material materials with Dissipation factor, 1MHz of 0.03 [-] | IEC 62631-2-1 |
Kriechstromfestigkeit | 23.0 °C | 600 V Show Material materials with Kriechstromfestigkeit of 600 V | IEC 60112 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | IEC 62631-3-1 |
Rheological Properties
Technological properties
| Property |
|---|