Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.62 g/cm³ Show Material materials with Dichte of 1.62 g/cm³ | ISO 1183 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dehnung | 23.0 °C | 2 % Show Material materials with Dehnung of 2 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 6.2 GPa Show Material materials with Elastizitätsmodul of 6.2 GPa | ISO 527-1/-2 |
Poissonzahl | 23.0 °C | 0.35 [-] Show Material materials with Poissonzahl of 0.35 [-] | |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 2.5 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 2.5 kJ/m² | ISO 179/1eA |
Schlagzähigkeit, Charpy ungekerbt | -6.0 °C | 20 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 20 kJ/m² | ISO 179/1eU |
23.0 °C | 20 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 20 kJ/m² | ISO 179/1eU | |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 2 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 2 kJ/m² | ISO 180/1A |
Zugfestigkeit | 23.0 °C | 65 MPa Show Material materials with Zugfestigkeit of 65 MPa | ISO 527-1/-2 |
Thermisch
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 145 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 145 °C | ISO 75-1/-2 | |
Relative temperature index, electrical | 120 °C Show Material materials with Relative temperature index, electrical of 120 °C | UL 746B | 120mil | |
Relative temperature index, mechanical impact | 115 °C Show Material materials with Relative temperature index, mechanical impact of 115 °C | UL 746B | 120mil | |
Relative temperature index, mechanical strength | 115 °C Show Material materials with Relative temperature index, mechanical strength of 115 °C | UL 746B | 120mil | |
Schmelzpunkt | 263 °C Show Material materials with Schmelzpunkt of 263 °C | ISO 11357-1/-3 | 18°F/min | |
Entflammbarkeit | Burning Behav. at 60mil nom. thickn.: V-0 class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: V-2 class, Thickness tested: 0.75 mm, UL recognition: yes -, Burning Behav. 5V at thickness h: 5VA class, Thickness tested: 1.5 mm, UL recognition: yes -, Oxygen index: 40 %, Glow Wire Flammability Index, 30mil: 960 °C, Glow Wire Flammability Index, 60mil: 960 °C, Glow Wire Flammability Index, 120mil: 960 °C, Glow Wire Ignition Temperature, 30mil: 800 °C, Glow Wire Ignition Temperature, 40mil: 800 °C, Glow Wire Ignition Temperature, 60mil: 800 °C, Glow Wire Ignition Temperature, 120mil: 800 °C, FMVSS Class: DNI - |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 30% Mineral Powder | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 295°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |