Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.09 g/cm³ Show Material materials with Dichte of 1.09 g/cm³ | ISO 1183 |
Mechanisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Dehnung | 23.0 °C | 38 % Show Material materials with Dehnung of 38 % | ISO 527-1/-2 | ||
Elastizitätsmodul | 23.0 °C | 2 GPa Show Material materials with Elastizitätsmodul of 2 GPa | ISO 527-1/-2 | ||
Elongation at yield | 23.0 °C | 6 % Show Material materials with Elongation at yield of 6 % | ISO 527-1/-2 | ||
Poissonzahl | 23.0 °C | 0.4 [-] Show Material materials with Poissonzahl of 0.4 [-] | |||
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 72 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 72 kJ/m² | ISO 179/1eA | ||
Streckgrenze | 23.0 °C | 51 MPa Show Material materials with Streckgrenze of 51 MPa | ISO 527-1/-2 | ||
Schlagzähigkeit, Charpy ungekerbt | No Break @ 23°C, ISO 179/1eU |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 61 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 61 °C | ISO 75-1/-2 | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.1E-4 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.1E-4 1/K | ISO 11359-1/-2 | ||
Relative temperature index, electrical | 130 °C Show Material materials with Relative temperature index, electrical of 130 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 105 °C Show Material materials with Relative temperature index, mechanical impact of 105 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 110 °C Show Material materials with Relative temperature index, mechanical strength of 110 °C | UL 746B | 120mil | |||
Schmelzpunkt | 263 °C Show Material materials with Schmelzpunkt of 263 °C | ISO 11357-1/-3 | 18°F/min | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1.2E-4 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.2E-4 1/K | ISO 11359-1/-2 | ||
Entflammbarkeit | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, UL recognition: yes -, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 290°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Max. screw tangential speed: 0.3m/s, Mold Temperature Optimum: 80°C, Min. mold temperature: 50°C, Max. mold temperature: 100°C, Hold pressure range: 50-100MPa, Hold pressure time: 4s/mm, Ejection temperature: 190°C |