Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.01 g/cm³ Show Material materials with Dichte of 1.01 g/cm³ | ISO 1183 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dehnung | 23.0 °C | 100 % Show Material materials with Dehnung of 100 % | ISO 527-1/-2 | 50mm/min |
Elastizitätsmodul | 23.0 °C | 1.1 GPa Show Material materials with Elastizitätsmodul of 1.1 GPa | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 12 % Show Material materials with Elongation at yield of 12 % | ISO 527-1/-2 |
Härte, Shore D | 23.0 °C | 69 [-] Show Material materials with Härte, Shore D of 69 [-] | ISO 7619-1 | 15 seconds |
Poissonzahl | 23.0 °C | 0.45 [-] Show Material materials with Poissonzahl of 0.45 [-] | |
Schlagfestigkeit, Charpy gekerbt | -6.0 °C | 13 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 13 kJ/m² | ISO 179/1eA |
23.0 °C | 35 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 35 kJ/m² | ISO 179/1eA | |
Streckgrenze | 23.0 °C | 32 MPa Show Material materials with Streckgrenze of 32 MPa | ISO 527-1/-2 |
Thermisch
| Property | Value | Comment | |
|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 83 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 83 °C | ISO 75-1/-2 | |
Heat deflection temperature, 1.80 MPa | 47 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 47 °C | ISO 75-1/-2 | |
Schmelzpunkt | 216 °C Show Material materials with Schmelzpunkt of 216 °C | ISO 11357-1/-3 | 18°F/min | |
Entflammbarkeit | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min | ||
Technological properties
| Property |
|---|