Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.39 g/cm³ Show Material materials with Dichte of 1.39 g/cm³ | ISO 1183 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dehnung | 23.0 °C | 3.5 % Show Material materials with Dehnung of 3.5 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 10 GPa Show Material materials with Elastizitätsmodul of 10 GPa | ISO 527-1/-2 |
Poissonzahl | 23.0 °C | 0.34 [-] Show Material materials with Poissonzahl of 0.34 [-] | |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 14 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 14 kJ/m² | ISO 179/1eA |
Schlagzähigkeit, Charpy ungekerbt | 23.0 °C | 95 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 95 kJ/m² | ISO 179/1eU |
Schlagzähigkeit, Izod ungekerbt | -40.0 °C | 10 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 10 kJ/m² | ISO 180/1A |
Zugfestigkeit | 23.0 °C | 185 MPa Show Material materials with Zugfestigkeit of 185 MPa | ISO 527-1/-2 |
Thermisch
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 220 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 220 °C | ISO 75-1/-2 | |
Relative temperature index, electrical | 65 °C Show Material materials with Relative temperature index, electrical of 65 °C | UL 746B | 120mil | |
Relative temperature index, mechanical impact | 65 °C Show Material materials with Relative temperature index, mechanical impact of 65 °C | UL 746B | 120mil | |
Relative temperature index, mechanical strength | 65 °C Show Material materials with Relative temperature index, mechanical strength of 65 °C | UL 746B | 120mil | |
Schmelzpunkt | 250 °C Show Material materials with Schmelzpunkt of 250 °C | ISO 11357-1/-3 | 18°F/min | |
Entflammbarkeit | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.81 mm, UL recognition: yes -, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 33% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 290°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |