Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.39 g/cm³ Show Material materials with Dichte of 1.39 g/cm³ | ISO 1183 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegemodul | 23.0 °C | 8.9 GPa Show Material materials with Biegemodul of 8.9 GPa | ISO 178 |
Dehnung | 23.0 °C | 4 % Show Material materials with Dehnung of 4 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 10.9 GPa Show Material materials with Elastizitätsmodul of 10.9 GPa | ISO 527-1/-2 |
Poissonzahl | 23.0 °C | 0.34 [-] Show Material materials with Poissonzahl of 0.34 [-] | |
Schlagfestigkeit, Charpy gekerbt | -40.0 °C | 12.3 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 12.3 kJ/m² | ISO 179/1eA |
-6.0 °C | 10 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | ISO 179/1eA | |
23.0 °C | 16 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 16 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | 23.0 °C | 95 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 95 kJ/m² | ISO 179/1eU |
Zugfestigkeit | 23.0 °C | 194 MPa Show Material materials with Zugfestigkeit of 194 MPa | ISO 527-1/-2 |
Thermisch
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 225 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 225 °C | ISO 75-1/-2 | |
Schmelzpunkt | 245 °C Show Material materials with Schmelzpunkt of 245 °C | ISO 11357-1/-3 | 18°F/min | |
Entflammbarkeit | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 33% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 290°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |