Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.45 g/cm³ Show Material materials with Dichte of 1.45 g/cm³ | ISO 1183 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 216 MPa Show Material materials with Biegefestigkeit of 216 MPa | ISO 178 |
Biegemodul | 23.0 °C | 11.2 GPa Show Material materials with Biegemodul of 11.2 GPa | ISO 178 |
Dehnung | 23.0 °C | 1.8 % Show Material materials with Dehnung of 1.8 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 10.6 GPa Show Material materials with Elastizitätsmodul of 10.6 GPa | ISO 527-1/-2 |
Poissonzahl | 23.0 °C | 0.34 [-] Show Material materials with Poissonzahl of 0.34 [-] | |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 7 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 7 kJ/m² | ISO 179/1eA |
Schlagzähigkeit, Charpy ungekerbt | 23.0 °C | 46 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 46 kJ/m² | ISO 179/1eU |
Zugfestigkeit | 23.0 °C | 138 MPa Show Material materials with Zugfestigkeit of 138 MPa | ISO 527-1/-2 |
Thermisch
| Property | Value | Comment | |
|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 276 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 276 °C | ISO 75-1/-2 | annealed | |
Relative temperature index, electrical | 130 °C Show Material materials with Relative temperature index, electrical of 130 °C | UL 746B | 120mil | |
Relative temperature index, mechanical impact | 120 °C Show Material materials with Relative temperature index, mechanical impact of 120 °C | UL 746B | 120mil | |
Relative temperature index, mechanical strength | 130 °C Show Material materials with Relative temperature index, mechanical strength of 130 °C | UL 746B | 120mil | |
Schmelzpunkt | 315 °C Show Material materials with Schmelzpunkt of 315 °C | ISO 11357-1/-3 | first heat | |
Entflammbarkeit | Burning Behav. at thickness h: V-0 class, Thickness tested: 0.4 mm, UL recognition: yes -, Glow Wire Flammability Index, 15mil: 960 °C, Glow Wire Flammability Index, 60mil: 960 °C, Glow Wire Flammability Index, 120mil: 960 °C, Glow Wire Ignition Temperature, 15mil: 750 °C, Glow Wire Ignition Temperature, 60mil: 800 °C, Glow Wire Ignition Temperature, 120mil: 825 °C | ||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Kriechstromfestigkeit | 23.0 °C | 600 V Show Material materials with Kriechstromfestigkeit of 600 V | IEC 60112 |
Technological properties
| Property | ||
|---|---|---|
| Fillers | 30% Glass Fiber | |
| Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 6-8h, Processing Moisture Content: ≤0.1%, Min. melt temperature: 330°C, Max. melt temperature: 335°C, Min. mold temperature: 110°C, Max. mold temperature: 130°C | |