Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.6 - 1.8 g/cm³ Show Material materials with Dichte of 1.6 - 1.8 g/cm³ | observed density |
Wasserabsorption | 23.0 °C | 0.03 % Show Material materials with Wasserabsorption of 0.03 % |
Mechanisch
| Property | Temperature | Value |
|---|---|---|
Biegefestigkeit | 23.0 °C | 100 MPa Show Material materials with Biegefestigkeit of 100 MPa |
Biegemodul | 23.0 °C | 15.2 GPa Show Material materials with Biegemodul of 15.2 GPa |
Druckfestigkeit | 23.0 °C | 110 MPa Show Material materials with Druckfestigkeit of 110 MPa |
Hardness, Rockwell R | 23.0 °C | 121 [-] Show Material materials with Hardness, Rockwell R of 121 [-] |
Impact strength, Izod notched, ASTM | 23.0 °C | 32 J/m Show Material materials with Impact strength, Izod notched, ASTM of 32 J/m |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 101 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 101 J/m |
Streckgrenze | 23.0 °C | 74 MPa Show Material materials with Streckgrenze of 74 MPa |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Glasübergangstemperatur | 84.85 °C Show Material materials with Glasübergangstemperatur of 84.85 °C | DSC | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 2.8E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.8E-5 1/K | |||
Schmelzpunkt | 284.85 °C Show Material materials with Schmelzpunkt of 284.85 °C | DSC | |||
Wärmeformbeständigkeitstemperatur | 259.85 °C Show Material materials with Wärmeformbeständigkeitstemperatur of 259.85 °C | min. | |||
Wärmeleitfähigkeit | 23.0 °C | 0.29 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 0.29 W/(m·K) | |||
Entflammbarkeit | V-0/5V | ||||
Elektrisch
| Property | Temperature | Value |
|---|---|---|
Dielektrizitätskonstante | 23.0 °C | 4.6 [-] Show Material materials with Dielektrizitätskonstante of 4.6 [-] |
Durchschlagfestigkeit | 23.0 °C | 13.4 - 15.7 kV/mm Show Material materials with Durchschlagfestigkeit of 13.4 - 15.7 kV/mm |
Kriechstromfestigkeit | 23.0 °C | 235 V Show Material materials with Kriechstromfestigkeit of 235 V |
Verlustfaktor | 23.0 °C | 0.02 [-] Show Material materials with Verlustfaktor of 0.02 [-] |
spezifischer Widerstand | 23.0 °C | 2.00E+14 Ω·m Show Material materials with spezifischer Widerstand of 2.00E+14 Ω·m |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Poly( p-phenylene sulfide) (PPS) is mainly used in the reinforced form with glass fiber or mineral fillers as a high-performance thermoplastic. It is used for electrical and electronic parts (e.g., plugs and multipoint connectors, bobbins, relays, switches, encapsulation of electronic component, etc.), automobile parts (air intake systems, pumps, valves, gaskets, components for exhaust gas recirculation systems, etc.), and as components for mechanical and precision engineering. Nonfiller PPS is used for fiber, film, sheet, nonwoven fabric, etc. | |
| Fillers | Glass Fiber and Mineral Powder | |