Allgemein
Property | Value |
---|---|
Porosität | 2.64 - 2.68 % Show Material materials with Porosität of 2.64 - 2.68 % |
Mechanisch
Property | Temperature | Value |
---|---|---|
Biegefestigkeit | 23.0 °C | 33.7 MPa Show Material materials with Biegefestigkeit of 33.7 MPa |
Druckfestigkeit | 23.0 °C | 103 MPa Show Material materials with Druckfestigkeit of 103 MPa |
Härte, Mohs | 23.0 °C | 5 [-] Show Material materials with Härte, Mohs of 5 [-] |
Zugfestigkeit | 23.0 °C | 23.4 MPa Show Material materials with Zugfestigkeit of 23.4 MPa |
Thermisch
Property | Temperature | Value |
---|---|---|
Koeffizient der thermischen Ausdehnung | 600.0 °C | 2.9E-6 - 3.5E-6 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.9E-6 - 3.5E-6 1/K |
Vicat-Erweichungstemperatur | 1600 °C Show Material materials with Vicat-Erweichungstemperatur of 1600 °C | |
Wärmeleitfähigkeit | 23.0 °C | 1.5 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 1.5 W/(m·K) |
Technological properties
Property | ||
---|---|---|
Chemical composition | Silica - 56.8%, Alumina - 33.37%, Ferric oxide - 0.79%, Titanium Dioxide - 2.42%, Calcium Oxide - 0.29%, Magnesium Oxide - 0.24% | |
Color | Pink to dark brown | |
Other | Typical characteristics of the Pyrophyllite material include: Machinable, thermally insulating, good thermal shock properties, good mechanical stability once fired. Typical characteristics of the Pyrophyllite material include: Machinable, thermally insulating, good thermal shock properties, good mechanical stability once fired. The key features of Pyrophyllite Heat Treated at 800 °C - 1000 °C are: Poor heat conductivity (Thermal insulator), good resistance to thermal shock, low coefficient of thermal expansion, good mechanical stability, can still be machined for final sizes with Tungsten carbide tools. When fired to 800 °C - 1000 °C around 1.75 - 2.0 % expansion occurs and must be allowed for when machining, however when fired to these temperatures sizes can be adjusted with carbide tools. Components fired to 1000 °C can be operated continuously at that temperature. |