Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.17 g/cm³ Show Material materials with Dichte of 1.17 g/cm³ | ASTM D792 |
Wasserabsorption | 23.0 °C | 1.6 % Show Material materials with Wasserabsorption of 1.6 % | for 54h to boiling water |
Mechanisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Biegefestigkeit | 23.0 °C | 152 MPa Show Material materials with Biegefestigkeit of 152 MPa | ASTM D790 | ||
Dehnung | 23.0 °C | 4 - 7.2 % Show Material materials with Dehnung of 4 - 7.2 % | |||
Elastizitätsmodul | 23.0 °C | 3.1 GPa Show Material materials with Elastizitätsmodul of 3.1 GPa | ASTM D638 | ||
Plane-Strain Fracture Toughnes | 23.0 °C | 0.62 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 0.62 MPa·√m | ASTM D5045 | ||
Zugfestigkeit | 23.0 °C | 95 MPa Show Material materials with Zugfestigkeit of 95 MPa | ASTM D638 | ||
Formänderungsenergieabgabe | ASTM D5045 | ||||
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Glasübergangstemperatur | 202 °C Show Material materials with Glasübergangstemperatur of 202 °C | ASTM E1640 | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 7.2E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 7.2E-5 1/K | ASTM E831 | ||
Max. Betriebstemperatur | 150 | ||||
Technological properties
| Property | ||
|---|---|---|
| Application areas | Drones;Sports equipment: Frame, wheels, seat, seat post, handlebar, head stem and crank arm of a sports bicycle are made of carbon composite;Geometry strengthen elements: Experimental stringer panel | |
| Processing history | Preheat the resin to 60-90°С in its container for transfer to the resin pot. Degas the resin for 30-40 minutes while heating to 90°С. Preheat the tool to 100-110°С (or to 115-120°С for parts having complex shape or for UD parts). Maintaining resin pot temperature of 95 °С and tool temperature of 100-115 °С, begin resin infusion. After complete impregnation increase tool temperature at 2°С/min to 180°С. Dwell at 180°С for 3 h. Cool the tool to 90°С at <5°С/min before releasing part from tool. | |
| Processing methods | Preheat the resin to 60-90°С in its container for transfer to the resin pot. Degas the resin for 30-40 minutes while heating to 90°С. Preheat the tool to 100-110°С (or to 115-120°С for parts having complex shape or for UD parts). Maintaining resin pot temperature of 95 °С and tool temperature of 100-115 °С, begin resin infusion. After complete impregnation increase tool temperature at 2°С/min to 180°С. Dwell at 180°С for 3 h. Cool the tool to 90°С at <5°С/min before releasing part from tool. | |