Structural Epoxy Resin T26 (EP-PCF)

Want to keep this datasheet? Save it now in your required format

Description

Т26 is a single part low viscosity epoxy infusion carbon fabric plasticized resin developed for high-loaded structures. T26 offers simple and flexible processing due to low viscosity at relatively low impregnation temperatures (110°С). T26 was developed specially for RTM and vacuum infusion molding, to produce laminates with low porosity and extremely high mechanical performance, especially in crack resistance. It shows the following features and properties:

One-part resin designed specifically for high-temperature infusion or RTM

Wide processing window > 7 hours at 110°C

Curing at 180°C provides glass transition temperature of 205°C

High wet glass transition temperature —172°C

Very high resistance to impact

Operating temperatures from –60°C to 150°C

Diese Materialdaten wurden von Matmatch zur Verfügung gestellt

Alle Daten beziehen sich auf Raumtemperatur soweit nicht anderweitig spezifiziert. SI Einheiten werden verwendt soweit nicht anderweitig spezifiziert.
Äquivalente Standards sind ähnlich zu einem oder mehreren Standards die der Anbieter angegeben hat. Manche äquivalente Standards können strikter sein oder außerhalb der Bedingungen des ursprünglichen Standards.

Ashby charts

All categories

Eigenschaften

Mechanisch

Property	Temperature	Value	Comment
Druckfestigkeit	23.0 °C	638 MPa Show Material materials with Druckfestigkeit of 638 MPa	ASTM D6641
Druckfestigkeit, transversal	23.0 °C	608 MPa Show Material materials with Druckfestigkeit, transversal of 608 MPa	ASTM D6641
Elastizitätsmodul	23.0 °C	66 GPa Show Material materials with Elastizitätsmodul of 66 GPa	ASTM D3039
Elastizitätsmodul, transversal	23.0 °C	66 GPa Show Material materials with Elastizitätsmodul, transversal of 66 GPa	ASTM D3039
Shear modulus, G₁₂	23.0 °C	4.3 GPa Show Material materials with Shear modulus, G₁₂ of 4.3 GPa	ASTM D5379
Shear strength, τ₁₂	23.0 °C	79 MPa Show Material materials with Shear strength, τ₁₂ of 79 MPa
Shear strength, τ₁₃	25.0 °C	66 MPa Show Material materials with Shear strength, τ₁₃ of 66 MPa	ASTM D2344
	120.0 °C	40 MPa Show Material materials with Shear strength, τ₁₃ of 40 MPa	ASTM D2344
	150.0 °C	34 MPa Show Material materials with Shear strength, τ₁₃ of 34 MPa	ASTM D2344

Zugfestigkeit	23.0 °C	904 MPa Show Material materials with Zugfestigkeit of 904 MPa	ASTM D3039
Zugfestigkeit, transversal	23.0 °C	904 MPa Show Material materials with Zugfestigkeit, transversal of 904 MPa	ASTM D3039
Formänderungsenergieabgabe	ASTM D5528

Technological properties

Property
Application areas	Drones;Sports equipment: Frame, wheels, seat, seat post, handlebar, head stem and crank arm of a sports bicycle are made of carbon composite;Geometry strengthen elements: Experimental stringer panel
Processing history	Samples for testing were obtained by vacuum infusion based on T26 resin and plasticized carbon fabric (PCF) 22508 covered by veil.
Processing methods	Preheat the resin to 60-90°С in its container for transfer to the resin pot. Degas the resin for 30-40 minutes while heating to 90°С. Preheat the tool to 100-110°С (or to 115-120°С for parts having complex shape or for UD parts). Maintaining resin pot temperature of 95 °С and tool temperature of 100-115 °С, begin resin infusion. After complete impregnation increase tool temperature at 2°С/min to 180°С. Dwell at 180°С for 3 h. Cool the tool to 90°С at <5°С/min before releasing part from tool.

Structural Epoxy Resin T26 (EP-PCF)

Description

Ashby charts

Anwendungen

Empfohlene Literatur

Eigenschaften