Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Compressive strength laminate | 25.0 °C | 708 MPa Show Material materials with Compressive strength laminate of 708 MPa | |
85.0 °C | 639 MPa Show Material materials with Compressive strength laminate of 639 MPa | ||
Druckfestigkeit | 23.0 °C | 802 MPa Show Material materials with Druckfestigkeit of 802 MPa | ASTM D6641, Lamina |
Elastizitätsmodul | 23.0 °C | 71 GPa Show Material materials with Elastizitätsmodul of 71 GPa | ASTM D3039, Lamina |
Kompressionsmodul | 23.0 °C | 60 MPa Show Material materials with Kompressionsmodul of 60 MPa | ASTM D695, Lamina |
Shear strength, τ₁₂ | 23.0 °C | 126 MPa Show Material materials with Shear strength, τ₁₂ of 126 MPa | |
Zugfestigkeit | 23.0 °C | 871 MPa Show Material materials with Zugfestigkeit of 871 MPa | ASTM D3039, Lamina |
Technological properties
Property | ||
---|---|---|
Application areas | Marine: The shells of boats and sport catamarans can be made of composites;Car tuning: The composite material provides solutions for automotive parts to be light-weighted, stylish and aesthetic;Sports equipment: Frame, wheels, seat, seat post, handlebar, head stem and crank arm of a sports bicycle are made of carbon composite | |
Processing history | Reinforcing filler: carbon fabric 22502 (twill 2x2, 200 g/m2, HTA40). Carbon plastic is produced by vacuum molding. | |
Processing methods | Holding at a temperature of 25-30°C, for 12 hours, a vacuum of -1 bar. Heating 2°C/min. up to 120°C, holding at 120°C for 180 minutes. Heating 2°C/min. up to 180°C, holding at 180°C for 180 minutes, cooling no faster than 5°C/min. up to 50°С. |