Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Wasserabsorption | 23.0 °C | 3.57 % Show Material materials with Wasserabsorption of 3.57 % | for 54h to boiling water |
Mechanisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Biegefestigkeit | 23.0 °C | 189 MPa Show Material materials with Biegefestigkeit of 189 MPa | ASTM D790 | ||
Plane-Strain Fracture Toughnes | 23.0 °C | 2.08 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 2.08 MPa·√m | ASTM D5045 | ||
Zugfestigkeit | 23.0 °C | 82 MPa Show Material materials with Zugfestigkeit of 82 MPa | ASTM D638 | ||
Formänderungsenergieabgabe | ASTM D5045 | ||||
Thermisch
| Property | Value | Comment |
|---|---|---|
Glasübergangstemperatur | 175 °C Show Material materials with Glasübergangstemperatur of 175 °C | ASTM E2092 |
Technological properties
| Property | ||
|---|---|---|
| Application areas | High-loaded automotive parts;Sports equipment: Bicycle, frame, wheels, seat, seat post, handlebar, head stem and crank arm of a sports bicycle are made of carbon composite;Geometry strengthen elements: Experimental stringer panel;High-loaded aircraft parts: Aircraft engine hoods | |
| Processing methods | Heating 2°С/min in 1 bar pressure up to 150°С. Then expose it for 30 min. Heating again at 2°С/min in 2 bar pressure up to 150°С. Then expose it for 180 min and pressure 3-6 bar. Last step is cooling with 5°С/min to 50°С. | |