Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.27 g/cm³ Show Material materials with Dichte of 1.27 g/cm³ | ASTM D792 |
Mechanisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Biegefestigkeit | 23.0 °C | 155 MPa Show Material materials with Biegefestigkeit of 155 MPa | ASTM D790 | ||
Elastizitätsmodul | 23.0 °C | 3.2 GPa Show Material materials with Elastizitätsmodul of 3.2 GPa | ASTM D638 | ||
Plane-Strain Fracture Toughnes | 23.0 °C | 0.76 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 0.76 MPa·√m | ASTM D5045 | ||
Zugfestigkeit | 23.0 °C | 80 MPa Show Material materials with Zugfestigkeit of 80 MPa | ASTM D638 | ||
Formänderungsenergieabgabe | ASTM D5045 |
Thermisch
Property | Value | Comment |
---|---|---|
Glasübergangstemperatur | 87 °C Show Material materials with Glasübergangstemperatur of 87 °C | ASTM E2092 |
Technological properties
Property | ||
---|---|---|
Application areas | Marine: The shells of boats and sport catamarans can be made of composite;Car tuning: The composite material provides solutions for automotive parts to be light-weighted, stylish and aesthetic;Wind energy: Wind turbines is usually made of carbon fiber plastic;Design;Room temperature tooling;High-pressure cylinders | |
Processing methods | Mix the components A and B and weight proportion 100:32. Degas the resin with intensive mixing for 15-20 minutes at 20-25°С. Maintaining resin pot temperature of 20-25°С and tool temperature of 20-25°С, begin resin infusion. Cure at room temperature for 24h. Make sure the resin is gelled. Remove auxiliary materials. Increase temperature at rate 0,5-2°С/min to 80°С. Postcure at 80°С for 3-6h. |