Eigenschaften
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Druckfestigkeit | 25.0 °C | 783 MPa Show Material materials with Druckfestigkeit of 783 MPa | ASTM D6641 |
120.0 °C | 623 MPa Show Material materials with Druckfestigkeit of 623 MPa | ASTM D6641 | |
Elastizitätsmodul | 23.0 °C | 62 GPa Show Material materials with Elastizitätsmodul of 62 GPa | ASTM D3039 |
Kompressionsmodul | 23.0 °C | 62 MPa Show Material materials with Kompressionsmodul of 62 MPa | ASTM D695 |
Shear modulus, G₁₂ | 23.0 °C | 4.9 GPa Show Material materials with Shear modulus, G₁₂ of 4.9 GPa | ASTM D5379 |
Shear strength, τ₁₂ | 23.0 °C | 106 MPa Show Material materials with Shear strength, τ₁₂ of 106 MPa | |
Shear strength, τ₁₃ | 25.0 °C | 81 MPa Show Material materials with Shear strength, τ₁₃ of 81 MPa | ASTM D2344 |
90.0 °C | 73 MPa Show Material materials with Shear strength, τ₁₃ of 73 MPa | ASTM D2344 | |
120.0 °C | 66 MPa Show Material materials with Shear strength, τ₁₃ of 66 MPa | ASTM D2344 | |
150.0 °C | 57 MPa Show Material materials with Shear strength, τ₁₃ of 57 MPa | ASTM D2344 | |
Zugfestigkeit | 23.0 °C | 904 MPa Show Material materials with Zugfestigkeit of 904 MPa | ASTM D3039 |
Technological properties
| Property | ||
|---|---|---|
| Application areas | High-loaded automotive parts;Sports equipment: Bicycle, frame, wheels, seat, seat post, handlebar, head stem and crank arm of a sports bicycle are made of carbon composite;Geometry strengthen elements: Experimental stringer panel;High-loaded aircraft parts: Aircraft engine hoods | |
| Processing history | Samples for testing were obtained by vacuum infusion based on T60-180 resin and carbon fabric 22502 (twill 2x2, 200 g/m2, 3K, 3.95 GPa). | |
| Processing methods | Heating 2°С/min in 1 bar pressure up to 150°С. Then expose it for 30 min. Heating again at 2°С/min in 2 bar pressure up to 150°С. Then expose it for 180 min and pressure 3-6 bar. Last step is cooling with 5°С/min to 50°С. | |