Eigenschaften
Allgemein
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Dichte | 20.0 °C | 4.43 g/cm³ Show Material materials with Dichte of 4.43 g/cm³ | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |
Mechanisch
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Dehnung | 20.0 °C | 8.0 % Show Material materials with Dehnung of 8.0 % | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | Rod, Forging |
Elastizitätsmodul | -269.0 °C | 119.6 GPa Show Material materials with Elastizitätsmodul of 119.6 GPa | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |
-195.0 °C | 118.2 GPa Show Material materials with Elastizitätsmodul of 118.2 GPa | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod | |
20.0 °C | 110.0 GPa Show Material materials with Elastizitätsmodul of 110.0 GPa | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod | |
27.0 °C | 109.2 GPa Show Material materials with Elastizitätsmodul of 109.2 GPa | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod | |
200.0 °C | 98.0 GPa Show Material materials with Elastizitätsmodul of 98.0 GPa | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod | |
400.0 °C | 84.0 GPa Show Material materials with Elastizitätsmodul of 84.0 GPa | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod | |
Flächenreduzierung | 20.0 °C | 15.0 % Show Material materials with Flächenreduzierung of 15.0 % | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | Rod, Forging |
20.0 °C | 20.0 % Show Material materials with Flächenreduzierung of 20.0 % | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | Forging | |
Härte, Brinell | 20.0 °C | 310.0 Show Material materials with Härte, Brinell of 310.0 | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | Rod |
Poissonzahl | -269.0 °C | 0.311 [-] Show Material materials with Poissonzahl of 0.311 [-] | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |
-195.0 °C | 0.327 [-] Show Material materials with Poissonzahl of 0.327 [-] | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod | |
27.0 °C | 0.333 [-] Show Material materials with Poissonzahl of 0.333 [-] | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod | |
Schubmodule | 20.0 °C | 43.0 GPa Show Material materials with Schubmodule of 43.0 GPa | Artificially Aged | WL 3.7164-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Forging, Rod |
Zugfestigkeit | 20.0 °C | 1060.0 MPa Show Material materials with Zugfestigkeit of 1060.0 MPa | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | Forging |
20.0 °C | 1070.0 MPa Show Material materials with Zugfestigkeit of 1070.0 MPa | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | Rod, Forging | |
20.0 °C | 1100.0 MPa Show Material materials with Zugfestigkeit of 1100.0 MPa | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | Forging, Rod | |
20.0 °C | 1180.0 MPa Show Material materials with Zugfestigkeit of 1180.0 MPa | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | ||
100.0 °C | 1090.0 MPa Show Material materials with Zugfestigkeit of 1090.0 MPa | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | ||
200.0 °C | 1000.0 MPa Show Material materials with Zugfestigkeit of 1000.0 MPa | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | ||
300.0 °C | 910.0 MPa Show Material materials with Zugfestigkeit of 910.0 MPa | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | ||
400.0 °C | 855.0 MPa Show Material materials with Zugfestigkeit of 855.0 MPa | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 | ||
500.0 °C | 735.0 MPa Show Material materials with Zugfestigkeit of 735.0 MPa | Artificially Aged | DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860 |
Thermisch
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 7.699999999999999e-06 - 1e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 7.699999999999999e-06 - 1e-05 1/K | Typical for Titanium Alpha Beta Alloy | ||||
Schmelzpunkt | 1500.0 - 1750.0 °C Show Material materials with Schmelzpunkt of 1500.0 - 1750.0 °C | Typical for Titanium Alpha Beta Alloy | ||||
Spezifische Wärmekapazität | 370.0 - 674.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 370.0 - 674.0 J/(kg·K) | Typical for Titanium Alpha Beta Alloy | ||||
Wärmeleitfähigkeit | 20.0 °C | 7.12 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 7.12 W/(m·K) | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |
Elektrisch
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
spezifischer Widerstand | 20.0 °C | 1.71e-06 Ω·m Show Material materials with spezifischer Widerstand of 1.71e-06 Ω·m | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Aluminium | 5.5 - 6.75 % Show Material materials with Aluminium of 5.5 - 6.75 % | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |
Eisen | 0.3 Show Material materials with Eisen of 0.3 | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |
Kohlenstoff | 0.08 Show Material materials with Kohlenstoff of 0.08 | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |
Sauerstoff | 0.2 Show Material materials with Sauerstoff of 0.2 | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |
Stickstoff | 0.05 Show Material materials with Stickstoff of 0.05 | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |
Titan | 87.7 % Show Material materials with Titan of 87.7 % | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |
Vanadium | 3.5 - 4.5 % Show Material materials with Vanadium of 3.5 - 4.5 % | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |
Wasserstoff | 0.015 Show Material materials with Wasserstoff of 0.015 | Artificially Aged | DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860 | Forging, Rod |