DIN 1725-1 Grade 3.3207 T5

Want to keep this datasheet? Save it now in your required format

Description

E-AlMgSi0,5 is ensured by the German electrotechnical commission as alloy for electro-technology according to DIN 40 501 part of 1 to part of 4. This cold and hothardenable material reaches mechanical strength in range of 200 to 250 MPa with A5-elongation at break of approx. 10 %. In hot and/or cold hardend state is this alloy only limited formable, in the soft material condition however well. Weldability, corrosion resistance and anodising ability of this material are good. Heat treatment for hardening: solution annealing: 525 to 540 °C, quenching on air or in water cold ageing: 5 to 8 d at ambient temperatures warm ageing: 4 to 16 h at 155 to 190 °C. Application: The alloy E-AlMgSi0,5 is used with priority for bus bars. Because of the good extruding bar of this material as flat -, profile or tubing bus bars. Electro-technology (bus bars)

Related Standards

Equivalent Materials

Diese Materialdaten wurden von WIAM zur Verfügung gestellt

Alle Daten beziehen sich auf Raumtemperatur soweit nicht anderweitig spezifiziert. SI Einheiten werden verwendt soweit nicht anderweitig spezifiziert.
Äquivalente Standards sind ähnlich zu einem oder mehreren Standards die der Anbieter angegeben hat. Manche äquivalente Standards können strikter sein oder außerhalb der Bedingungen des ursprünglichen Standards.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Eigenschaften

Allgemein

Property	Temperature	Value	Condition	Related Standards	Shape
Dichte	20.0 °C	2.7 g/cm³ Show Material materials with Dichte of 2.7 g/cm³	T5	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod, Tube

Mechanisch

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Dehnung	20.0 °C	8.0 % Show Material materials with Dehnung of 8.0 %	T5	DIN 1725-1, EN 573-3, EN 573-4	Tube
	20.0 °C	10.0 % Show Material materials with Dehnung of 10.0 %	T5	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod, Tube	A10
	20.0 °C	12.0 % Show Material materials with Dehnung of 12.0 %	T5	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod, Tube
Elastizitätsmodul		70.0 GPa Show Material materials with Elastizitätsmodul of 70.0 GPa				Typical for Wrought 6000 Series Aluminium
Härte, Brinell	20.0 °C	45.0 - 65.0 [-] Show Material materials with Härte, Brinell of 45.0 - 65.0 [-]	T5	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod
	20.0 °C	65.0 - 90.0 [-] Show Material materials with Härte, Brinell of 65.0 - 90.0 [-]	T5	DIN 1725-1, EN 573-3, EN 573-4	Rod
	20.0 °C	65.0 - 80.0 [-] Show Material materials with Härte, Brinell of 65.0 - 80.0 [-]	T5	DIN 1725-1, EN 573-3, EN 573-4	Tube
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m				Typical for Wrought 6000 Series Aluminium
Poissonzahl		0.33 [-] Show Material materials with Poissonzahl of 0.33 [-]				Typical for Wrought 6000 Series Aluminium
Schubmodule	20.0 °C	25.5 GPa Show Material materials with Schubmodule of 25.5 GPa	T5	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod, Tube
Zugfestigkeit	20.0 °C	170.0 - 220.0 MPa Show Material materials with Zugfestigkeit of 170.0 - 220.0 MPa	T5	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod
	20.0 °C	215.0 - 280.0 MPa Show Material materials with Zugfestigkeit of 215.0 - 280.0 MPa	T5	DIN 1725-1, EN 573-3, EN 573-4	Rod, Tube

Thermisch

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Koeffizient der thermischen Ausdehnung		1.6e-05 - 2.4e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.6e-05 - 2.4e-05 1/K				Typical for Wrought 6000 Series Aluminium
Schmelzpunkt		555.0 - 655.0 °C Show Material materials with Schmelzpunkt of 555.0 - 655.0 °C				Typical for Wrought 6000 Series Aluminium
Spezifische Wärmekapazität	20.0 °C	898.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 898.0 J/(kg·K)	T5	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod, Tube
Wärmeleitfähigkeit	20.0 °C	220.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 220.0 W/(m·K)	T5	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod, Tube

Elektrisch

Property	Value	Comment
Elektrische Leitfähigkeit	21000000.0 - 34000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 21000000.0 - 34000000.0 S/m	Typical for Wrought 6000 Series Aluminium
spezifischer Widerstand	2.9e-08 - 5e-08 Ω·m Show Material materials with spezifischer Widerstand of 2.9e-08 - 5e-08 Ω·m	Typical for Wrought 6000 Series Aluminium

Chemical properties

Property	Value	Condition	Related Standards	Shape
Eisen	0.1 - 0.3 % Show Material materials with Eisen of 0.1 - 0.3 %	T5	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod, Tube
Kupfer	0.05 Show Material materials with Kupfer of 0.05	T5	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod, Tube
Magnesium	0.35 - 0.6 % Show Material materials with Magnesium of 0.35 - 0.6 %	T5	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod, Tube
Mangan	0.05 Show Material materials with Mangan of 0.05	T5	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod, Tube
Silizium	0.3 - 0.6 % Show Material materials with Silizium of 0.3 - 0.6 %	T5	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod, Tube
Zink	0.1 Show Material materials with Zink of 0.1	T5	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod, Tube

Technological properties

Property

Workability

Excellent workability.