DIN 1725-1 Grade 3.2316 T6

Want to keep this datasheet? Save it now in your required format

Description

This cold and hot hardenable material reaches mechanical strength of 200 to 250 MPa with A5-elongation at break of approx. 10 %. In warm and/or cold-hardened condition is this alloy only limited formable, in the soft material condition however well. Weldability, corrosion resistance and anodisingability of this material are good. However this alloy is used more for rivet or bolt joints, because of the destabilization danger in the welding zone. Heat treatment for hardening: solution annealing: 525 to 540 °C, quenching on air or in water cold ageing: 5 to 8 d at ambient temperature hot ageing: 4 to 16 h at 155 to 190 °C Application: In the construction of vehicles for vehicle floors, stands, commercial motor vehicle superstructures of all kinds, trim. In the building industry for window, doors, window walls, shower cubicles, fences. In the building of rail-mounted vehicles for car boxes. In shipbuilding for sail masts, sail trees. In mechanical engineering (including building of forms) and for metal goods (e.g. building fittings, table-ware, flow pressed parts, reflectors).

Related Standards

Equivalent Materials

Diese Materialdaten wurden von WIAM zur Verfügung gestellt

Alle Daten beziehen sich auf Raumtemperatur soweit nicht anderweitig spezifiziert. SI Einheiten werden verwendt soweit nicht anderweitig spezifiziert.
Äquivalente Standards sind ähnlich zu einem oder mehreren Standards die der Anbieter angegeben hat. Manche äquivalente Standards können strikter sein oder außerhalb der Bedingungen des ursprünglichen Standards.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Eigenschaften

Allgemein

Property	Temperature	Value	Condition	Related Standards	Shape
Dichte	20.0 °C	2.7 g/cm³ Show Material materials with Dichte of 2.7 g/cm³	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging

Mechanisch

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Dehnung	20.0 °C	8.0 % Show Material materials with Dehnung of 8.0 %	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging
Elastizitätsmodul	20.0 °C	73.0 Show Material materials with Elastizitätsmodul of 73.0	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging
Härte, Brinell	20.0 °C	75.0 [-] Show Material materials with Härte, Brinell of 75.0 [-]	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m				Typical for Wrought 6000 Series Aluminium
Poissonzahl		0.33 [-] Show Material materials with Poissonzahl of 0.33 [-]				Typical for Wrought 6000 Series Aluminium
Schubmodule	20.0 °C	27.0 Show Material materials with Schubmodule of 27.0	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging
Zugfestigkeit	20.0 °C	275.0 MPa Show Material materials with Zugfestigkeit of 275.0 MPa	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging

Thermisch

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Koeffizient der thermischen Ausdehnung		1.6e-05 - 2.4e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.6e-05 - 2.4e-05 1/K				Typical for Wrought 6000 Series Aluminium
Schmelzpunkt		555.0 - 655.0 °C Show Material materials with Schmelzpunkt of 555.0 - 655.0 °C				Typical for Wrought 6000 Series Aluminium
Spezifische Wärmekapazität		887.0 - 963.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 887.0 - 963.0 J/(kg·K)				Typical for Wrought 6000 Series Aluminium
Wärmeleitfähigkeit	20.0 °C	170.0 - 220.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 170.0 - 220.0 W/(m·K)	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging

Elektrisch

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Elektrische Leitfähigkeit	20.0 °C	24000000.0 - 32000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 24000000.0 - 32000000.0 S/m	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging
spezifischer Widerstand		2.9e-08 - 5e-08 Ω·m Show Material materials with spezifischer Widerstand of 2.9e-08 - 5e-08 Ω·m				Typical for Wrought 6000 Series Aluminium

Chemical properties

Property	Value	Condition	Related Standards	Shape
Chrom	0.03 Show Material materials with Chrom of 0.03	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging
Eisen	0.25 Show Material materials with Eisen of 0.25	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging
Kupfer	0.05 Show Material materials with Kupfer of 0.05	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging
Magnesium	0.6 - 0.7 % Show Material materials with Magnesium of 0.6 - 0.7 %	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging
Mangan	0.15 Show Material materials with Mangan of 0.15	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging
Silizium	0.8 - 1.0 % Show Material materials with Silizium of 0.8 - 1.0 %	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging
Titan	0.05 Show Material materials with Titan of 0.05	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging
Zink	0.1 Show Material materials with Zink of 0.1	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging

Technological properties

Property

Workability

Excellent workability.