Allgemein
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Dichte | 20.0 °C | 2.64 g/cm³ Show Material materials with Dichte of 2.64 g/cm³ | H32 | WL 3.3354, DIN 1725-1 | Wire |
Mechanisch
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Elastizitätsmodul | 20.0 °C | 71.0 GPa Show Material materials with Elastizitätsmodul of 71.0 GPa | H32 | WL 3.3354, DIN 1725-1 | Wire | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||||
Scherfestigkeit | 20.0 °C | 170.0 MPa Show Material materials with Scherfestigkeit of 170.0 MPa | H32 | WL 3.3354, DIN 1725-1 | Wire | Transverse |
20.0 °C | 170.0 - 193.0 MPa Show Material materials with Scherfestigkeit of 170.0 - 193.0 MPa | H32 | WL 3.3354, DIN 1725-1 | Transverse | ||
20.0 °C | 170.0 MPa Show Material materials with Scherfestigkeit of 170.0 MPa | H32 | WL 3.3354, DIN 1725-1 | Wire | ||
20.0 °C | 193.0 MPa Show Material materials with Scherfestigkeit of 193.0 MPa | H32 | WL 3.3354, DIN 1725-1 | Transverse | ||
Schubmodule | 26.0 - 26.5 GPa Show Material materials with Schubmodule of 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||||
Zugfestigkeit | 20.0 °C | 300.0 - 360.0 MPa Show Material materials with Zugfestigkeit of 300.0 - 360.0 MPa | H32 | WL 3.3354, DIN 1725-1 | Wire |
Thermisch
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 2.2e-05 - 2.5e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.2e-05 - 2.5e-05 1/K | Typical for Wrought 5000 Series Aluminium | ||||
Max. Betriebstemperatur | 150.0 °C Show Material materials with Max. Betriebstemperatur of 150.0 °C | Typical for Wrought 5000 Series Aluminium | ||||
Schmelzpunkt | 560.0 - 655.0 °C Show Material materials with Schmelzpunkt of 560.0 - 655.0 °C | Typical for Wrought 5000 Series Aluminium | ||||
Spezifische Wärmekapazität | 20.0 °C | 904.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 904.0 J/(kg·K) | H32 | WL 3.3354, DIN 1725-1 | Wire | |
Wärmeleitfähigkeit | 20.0 °C | 110.0 - 140.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 110.0 - 140.0 W/(m·K) | H32 | WL 3.3354, DIN 1725-1 | Wire |
Elektrisch
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Elektrische Leitfähigkeit | 20.0 °C | 15000000.0 - 19000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 15000000.0 - 19000000.0 S/m | H32 | WL 3.3354, DIN 1725-1 | Wire | |
spezifischer Widerstand | 3.3e-08 - 5e-08 Ω·m Show Material materials with spezifischer Widerstand of 3.3e-08 - 5e-08 Ω·m | Typical for Wrought 5000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chrom | 0.2 Show Material materials with Chrom of 0.2 | H32 | WL 3.3354, DIN 1725-1 | Wire |
Eisen | 0.5 Show Material materials with Eisen of 0.5 | H32 | WL 3.3354, DIN 1725-1 | Wire |
Kupfer | 0.1 Show Material materials with Kupfer of 0.1 | H32 | WL 3.3354, DIN 1725-1 | Wire |
Magnesium | 4.5 - 5.6 % Show Material materials with Magnesium of 4.5 - 5.6 % | H32 | WL 3.3354, DIN 1725-1 | Wire |
Mangan | 0.1 - 0.6 % Show Material materials with Mangan of 0.1 - 0.6 % | H32 | WL 3.3354, DIN 1725-1 | Wire |
Silizium | 0.4 Show Material materials with Silizium of 0.4 | H32 | WL 3.3354, DIN 1725-1 | Wire |
Zink | 0.2 Show Material materials with Zink of 0.2 | H32 | WL 3.3354, DIN 1725-1 | Wire |
Technological properties
| Property | ||
|---|---|---|
| Workability | Good workability. | |