DIN 1725-1 Grade 3.3354 H14

Want to keep this datasheet? Save it now in your required format

Description

The alloy is characterised by a good corrosion resistance. It is sea water steady and resistant to saline atmosphere. The Mg content increases the strength, but the cold forming capacity decreases. The material is nature hard, i.e. only by a cold forming and not by a purposeful heat treatment a strength increase can be attained. It is well polishable and anodisable. The splinter-giving machinability becomes better with increasing Mg content, just as the weldability. AlMg5 has the highest Mg content of the standardized AlMg alloys, so it is badly cold formable, but the strength is the highest, so that the employment is possible for statically more highly loaded constructions. The alloy is suitable for a splinter-giving machinig on automats. It possesses sensitivity to intergranular corrosion. By a purposeful heat treatment and/or by additive of Mn or Cr the inclination to the intergranular corrosion can be reduced. Application: In the optics, in the automobile engineering for body parts, in mechanical engineering (turned parts). For joining elements (solid rivets, blind rivets, riveting nuts and screws). In the building industry for carrying constructions as well as in shipbuilding considering the sensitivity to corrosion.

Related Standards

Equivalent Materials

Diese Materialdaten wurden von WIAM,AluKey zur Verfügung gestellt

Alle Daten beziehen sich auf Raumtemperatur soweit nicht anderweitig spezifiziert. SI Einheiten werden verwendt soweit nicht anderweitig spezifiziert.
Äquivalente Standards sind ähnlich zu einem oder mehreren Standards die der Anbieter angegeben hat. Manche äquivalente Standards können strikter sein oder außerhalb der Bedingungen des ursprünglichen Standards.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Eigenschaften

Allgemein

Property	Temperature	Value	Condition	Related Standards	Shape
Dichte		2.64 g/cm³ Show Material materials with Dichte of 2.64 g/cm³	H14	WL 3.3354	Wire
	20.0 °C	2.64 g/cm³ Show Material materials with Dichte of 2.64 g/cm³	H14	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire

Mechanisch

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Dehnung	-196.0 °C	33.0 % Show Material materials with Dehnung of 33.0 %	H14	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354
	-73.0 °C	25.0 % Show Material materials with Dehnung of 25.0 %	H14	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354
	20.0 °C	2.0 % Show Material materials with Dehnung of 2.0 %	H14	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Wire	A100
	20.0 °C	5.0 % Show Material materials with Dehnung of 5.0 %	H14	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire	A10
	20.0 °C	6.0 % Show Material materials with Dehnung of 6.0 %	H14	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube
	20.0 °C	18.5 % Show Material materials with Dehnung of 18.5 %	H14	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354
Elastizitätsmodul		71.0 GPa Show Material materials with Elastizitätsmodul of 71.0 GPa	H14	WL 3.3354	Wire
	20.0 °C	67.0 - 72.0 GPa Show Material materials with Elastizitätsmodul of 67.0 - 72.0 GPa	H14	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
Härte, Brinell	20.0 °C	80.0 [-] Show Material materials with Härte, Brinell of 80.0 [-]	H14	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m				Typical for Wrought 5000 Series Aluminium
Poissonzahl		0.33 [-] Show Material materials with Poissonzahl of 0.33 [-]				Typical for Wrought 5000 Series Aluminium
Schubmodule	20.0 °C	27.0 GPa Show Material materials with Schubmodule of 27.0 GPa	H14	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
Zugfestigkeit	-196.0 °C	495.0 MPa Show Material materials with Zugfestigkeit of 495.0 MPa	H14	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354
	-73.0 °C	340.0 MPa Show Material materials with Zugfestigkeit of 340.0 MPa	H14	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354
		300.0 - 360.0 MPa Show Material materials with Zugfestigkeit of 300.0 - 360.0 MPa	H14	WL 3.3354	Wire
	20.0 °C	280.0 MPa Show Material materials with Zugfestigkeit of 280.0 MPa	H14	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube
	20.0 °C	310.0 MPa Show Material materials with Zugfestigkeit of 310.0 MPa	H14	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Wire
	20.0 °C	330.0 MPa Show Material materials with Zugfestigkeit of 330.0 MPa	H14	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354

Thermisch

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Koeffizient der thermischen Ausdehnung	-50.0 °C	2.25e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.25e-05 1/K	H14	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
	20 °C	2.31e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.31e-05 1/K	H14	WL 3.3354	Wire
	100 °C	2.31e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.31e-05 1/K	H14	WL 3.3354	Wire
	100.0 °C	2.41e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.41e-05 1/K	H14	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
	200.0 °C	2.51e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.51e-05 1/K	H14	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
	300.0 °C	2.61e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.61e-05 1/K	H14	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
Max. Betriebstemperatur		150.0 °C Show Material materials with Max. Betriebstemperatur of 150.0 °C				Typical for Wrought 5000 Series Aluminium
Schmelzpunkt		565.0 - 640.0 °C Show Material materials with Schmelzpunkt of 565.0 - 640.0 °C	H14	WL 3.3354	Wire
Spezifische Wärmekapazität		904.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 904.0 J/(kg·K)	H14	WL 3.3354	Wire
	20.0 °C	904.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 904.0 J/(kg·K)	H14	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
Wärmeleitfähigkeit	20.0 °C	110.0 - 140.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 110.0 - 140.0 W/(m·K)	H14	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire

Elektrisch

Property	Temperature	Value	Condition	Related Standards	Shape
Elektrische Leitfähigkeit	20.0 °C	15000000.0 - 19000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 15000000.0 - 19000000.0 S/m	H14	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
spezifischer Widerstand		5.26e-08 - 6.67e-08 Ω·m Show Material materials with spezifischer Widerstand of 5.26e-08 - 6.67e-08 Ω·m	H14	WL 3.3354	Wire

Chemical properties

Property	Value	Condition	Related Standards	Shape
Chrom	0.2 % Show Material materials with Chrom of 0.2 %	H14	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
Eisen	0.5 % Show Material materials with Eisen of 0.5 %	H14	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
	0.50 % Show Material materials with Eisen of 0.50 %	H14	WL 3.3354	Wire
Kupfer	0.1 % Show Material materials with Kupfer of 0.1 %	H14	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
Magnesium	4.5 - 5.6 % Show Material materials with Magnesium of 4.5 - 5.6 %	H14	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
Mangan	0.1 - 0.6 % Show Material materials with Mangan of 0.1 - 0.6 %	H14	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
Silizium	0.4 % Show Material materials with Silizium of 0.4 %	H14	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
Titan	0.2 Show Material materials with Titan of 0.2	H14	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
Zink	0.2 % Show Material materials with Zink of 0.2 %	H14	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire

Technological properties

Property

Workability

Good workability.