EN 1563 Grade GJS-800-2 heat treatment by manufacturer or by agreement

EN-GJS-800-2 (before GGG-80 acc. to DIN 1693/01-73), a pearlitic cast iron with nodular graphite for cast parts of high strength and hardness, e.g. cutter heads, pinions, cast parts of high abrasion load, e.g. rabbles, worm wheel segments for construction machines. This cast iron mark applies to specimen made by machining of separately cast samples. The material is comparable to UNS F 36200 from the USA. The fracture toughness of this make accounts for 14 MPa*m^1/2 (information value). The fatigue strength (Woehler- rotating bending test) accounts for the unnotched specimen (diameter: 10,6 mm) 304 N/mm², for the notched sample 182 N/mm² (unnotched specimen: For annealed ferritic cast iron with nodular graphite (GGG) the fatigue strength approximates the tensile strength x0,5 (Rm) of GGG with a Rm of 370 N/mm². The rate decreases according to the increasing Rm so far until fatigue strength for perlitic and tempered GGG approximates Rm x0,4. The rate continues to increase if the Rm exceed 740 N/mm². Notched specimen: For a sample of 10,6 mm diameter at the notch and a circumferential 45°- V-notch at a radius of 0,25 mm the fatigue strength of annealed GGG increases to a value of the fatigue strength x approx.0,63 of unnotched samples of GGG with a Rm of 370 N/mm². This value decreases according to the rising Rm of ferritic GGG. For GGG of intermediate strength values and for perlitic GGG and for tempered GGG the fatigue strength of notched samples approximates fatigue strength x0,6 of unnotched samples). Pearlite resp. heat-treated martensite are the predominant structure.