EN 1652 Grade CuZn10 R240

Want to keep this datasheet? Save it now in your required format

Description

CuZn10 (CW501L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal conductivity is lower than for CuZn5. Favorable electrical conductivity. Corrosion resistance is similar to pure copper. Processing properties: warm forming: moderately cold forming: good machinability: unfavorable hard and soft soldering: very good TIG-welding: good burnishing: good CuZn10 is used in electrical engineering, for metal goods as well as in jewelry and watches industry, for projectile casings and as cladding and enamelling material. For the electrolytically tinned strip the coatings (Sn bright, Sn matt, Sn fuzed, SnPb) are listed by the application (better solderability, better corrosion resistance, reduction of the electrical contact resistance, better appearance) in the DIN EN 14436 : 2004-11 (Table 5)

Related Standards

Equivalent Materials

Diese Materialdaten wurden von WIAM zur Verfügung gestellt

Alle Daten beziehen sich auf Raumtemperatur soweit nicht anderweitig spezifiziert. SI Einheiten werden verwendt soweit nicht anderweitig spezifiziert.
Äquivalente Standards sind ähnlich zu einem oder mehreren Standards die der Anbieter angegeben hat. Manche äquivalente Standards können strikter sein oder außerhalb der Bedingungen des ursprünglichen Standards.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Empfohlene Literatur

Properties of Copper

Do you supply similar materials?

List your company on Matmatch now and reach engineers around the world looking for such materials.

Request more information

Eigenschaften

Allgemein

Property	Temperature	Value
Dichte	20.0 °C	8.79 - 8.8 g/cm³ Show Material materials with Dichte of 8.79 - 8.8 g/cm³

Mechanisch

Property	Temperature	Value
Dehnung	20.0 °C	45 - 47 % Show Material materials with Dehnung of 45 - 47 %
Dehnung A50	20.0 °C	36 % Show Material materials with Dehnung A50 of 36 %
Elastizitätsmodul	20.0 °C	124 GPa Show Material materials with Elastizitätsmodul of 124 GPa
	100.0 °C	123 GPa Show Material materials with Elastizitätsmodul of 123 GPa
	200.0 °C	118 GPa Show Material materials with Elastizitätsmodul of 118 GPa
	300.0 °C	113 GPa Show Material materials with Elastizitätsmodul of 113 GPa
	400.0 °C	107 GPa Show Material materials with Elastizitätsmodul of 107 GPa
	500.0 °C	98 GPa Show Material materials with Elastizitätsmodul of 98 GPa
	600.0 °C	88 GPa Show Material materials with Elastizitätsmodul of 88 GPa
	700.0 °C	78 GPa Show Material materials with Elastizitätsmodul of 78 GPa

Elongation A100	20.0 °C	43 % Show Material materials with Elongation A100 of 43 %
Elongation A11.3	20.0 °C	45 % Show Material materials with Elongation A11.3 of 45 %
Poissonzahl	20.0 °C	0.34 [-] Show Material materials with Poissonzahl of 0.34 [-]
Schubmodule	20.0 °C	46 GPa Show Material materials with Schubmodule of 46 GPa
Streckgrenze Rp 0,2	20.0 °C	140 - 150 MPa Show Material materials with Streckgrenze Rp 0,2 of 140 - 150 MPa
Zugfestigkeit	20.0 °C	240 - 290 MPa Show Material materials with Zugfestigkeit of 240 - 290 MPa

Thermisch

Property	Temperature	Value	Comment
Koeffizient der thermischen Ausdehnung	200.0 °C	1.9E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.9E-5 1/K
Schmelzpunkt		875 - 1075 °C Show Material materials with Schmelzpunkt of 875 - 1075 °C	Typical for Wrought Copper Brass
Spezifische Wärmekapazität	20.0 °C	376 - 377 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 376 - 377 J/(kg·K)
	100.0 °C	398 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 398 J/(kg·K)
	200.0 °C	410 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 410 J/(kg·K)
	300.0 °C	419 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 419 J/(kg·K)
	400.0 °C	431 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 431 J/(kg·K)
	500.0 °C	444 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 444 J/(kg·K)
	600.0 °C	452 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 452 J/(kg·K)
	700.0 °C	465 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 465 J/(kg·K)
	Unlock all property charts
Wärmeleitfähigkeit	20.0 °C	184 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 184 W/(m·K)
	80.0 °C	197 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 197 W/(m·K)
	120.0 °C	209 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 209 W/(m·K)
	160.0 °C	218 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 218 W/(m·K)
	200.0 °C	226 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 226 W/(m·K)
	Unlock all property charts

Elektrisch

Property	Temperature	Value
Elektrische Leitfähigkeit	20.0 °C	2.47E+7 - 2.50E+7 S/m Show Material materials with Elektrische Leitfähigkeit of 2.47E+7 - 2.50E+7 S/m
Specific Electrical conductivity		43 % IACS Show Material materials with Specific Electrical conductivity of 43 % IACS
spezifischer Widerstand	20.0 °C	4.1E-8 Ω·m Show Material materials with spezifischer Widerstand of 4.1E-8 Ω·m

Chemical properties

Property	Value
Aluminium	0.02 % Show Material materials with Aluminium of 0.02 %
Blei	0.05 % Show Material materials with Blei of 0.05 %
Eisen	0.05 % Show Material materials with Eisen of 0.05 %
Kupfer	89 - 91 % Show Material materials with Kupfer of 89 - 91 %
Nickel	0.3 % Show Material materials with Nickel of 0.3 %
Phosphor	0.2 % Show Material materials with Phosphor of 0.2 %
Zinn	0.1 % Show Material materials with Zinn of 0.1 %

Looking for suppliers of this material? Click to see 16 supplier of EN 1652 Grade CuZn10 R240 on Matmatch