Property | Temperature | Value |
---|---|---|
Dichte | 20.0 °C | 8.9 g/cm³ Show Material materials with Dichte of 8.9 g/cm³ |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dehnung | 20.0 °C | 30 % Show Material materials with Dehnung of 30 % | |
Elastizitätsmodul | 23.0 °C | 95 - 98 GPa Show Material materials with Elastizitätsmodul of 95 - 98 GPa | Typical for Wrought Copper Pure / Low Alloyed Copper |
Elongation A10 | 20.0 °C | 25 % Show Material materials with Elongation A10 of 25 % | |
Elongation A100 | 20.0 °C | 20 % Show Material materials with Elongation A100 of 20 % | |
Härte, Brinell | 20.0 °C | 40 - 60 [-] Show Material materials with Härte, Brinell of 40 - 60 [-] | |
Härte, Vickers | 20.0 °C | 40 - 80 [-] Show Material materials with Härte, Vickers of 40 - 80 [-] | |
Poissonzahl | 23.0 °C | 0.34 [-] Show Material materials with Poissonzahl of 0.34 [-] | Typical for Wrought Copper Pure / Low Alloyed Copper |
Schubmodule | 23.0 °C | 48 GPa Show Material materials with Schubmodule of 48 GPa | Typical for Wrought Copper Pure / Low Alloyed Copper |
Streckgrenze Rp 0,2 | 20.0 °C | 40 - 80 MPa Show Material materials with Streckgrenze Rp 0,2 of 40 - 80 MPa | |
Zugfestigkeit | 20.0 °C | 180 - 300 MPa Show Material materials with Zugfestigkeit of 180 - 300 MPa |
Thermisch
Property | Temperature | Value | Comment |
---|---|---|---|
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.6E-5 - 1.8E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.6E-5 - 1.8E-5 1/K | Typical for Wrought Copper Pure / Low Alloyed Copper |
Schmelzpunkt | 965 - 1100 °C Show Material materials with Schmelzpunkt of 965 - 1100 °C | Typical for Wrought Copper Pure / Low Alloyed Copper | |
Spezifische Wärmekapazität | 23.0 °C | 377 - 420 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 377 - 420 J/(kg·K) | Typical for Wrought Copper Pure / Low Alloyed Copper |
Chemical properties
Property | Value |
---|---|
Zirkonium | 0.1 - 0.2 % Show Material materials with Zirkonium of 0.1 - 0.2 % |