Eigenschaften
Allgemein
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Dichte | 2.77 g/cm³ Show Material materials with Dichte of 2.77 g/cm³ | T351 | ||
2.78 g/cm³ Show Material materials with Dichte of 2.78 g/cm³ | T351 | AA Standards, ASTM B209, ASTM B211 | ||
2.78 g/cm³ Show Material materials with Dichte of 2.78 g/cm³ | T351 | |||
2.79 g/cm³ Show Material materials with Dichte of 2.79 g/cm³ | T351 | Bar | ||
3.0 g/cm³ Show Material materials with Dichte of 3.0 g/cm³ | T351 |
Mechanisch
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Dehnung | -195 °C | 19 % Show Material materials with Dehnung of 19 % | T351 | Elongation in 50 mm | ||
-80 °C | 19 % Show Material materials with Dehnung of 19 % | T351 | Elongation in 50 mm | |||
3.0 % Show Material materials with Dehnung of 3.0 % | T351 | AA Standards, ASTM B209 | A100 | |||
5.0 % Show Material materials with Dehnung of 5.0 % | T351 | AA Standards, ASTM B209 | A100 | |||
6.0 % Show Material materials with Dehnung of 6.0 % | T351 | AA Standards, ASTM B209 | A100 | |||
7.0 % Show Material materials with Dehnung of 7.0 % | T351 | AA Standards, ASTM B209 | A100 | |||
8.0 % Show Material materials with Dehnung of 8.0 % | T351 | AA Standards, ASTM B211 | A100 | |||
9.0 % Show Material materials with Dehnung of 9.0 % | T351 | AA Standards, ASTM B211 | A100 | |||
10.0 % Show Material materials with Dehnung of 10.0 % | T351 | Bar | A50 | |||
12.0 % Show Material materials with Dehnung of 12.0 % | T351 | AA Standards, ASTM B209 | A50 | |||
13.0 % Show Material materials with Dehnung of 13.0 % | T351 | |||||
0 °C | 19 % Show Material materials with Dehnung of 19 % | T351 | Elongation in 50 mm | |||
20.0 % Show Material materials with Dehnung of 20.0 % | T351 | |||||
24 °C | 19 % Show Material materials with Dehnung of 19 % | T351 | Elongation in 50 mm | |||
100 °C | 19 % Show Material materials with Dehnung of 19 % | T351 | Elongation in 50 mm | |||
150 °C | 17 % Show Material materials with Dehnung of 17 % | T351 | Elongation in 50 mm | |||
205 °C | 27 % Show Material materials with Dehnung of 27 % | T351 | Elongation in 50 mm | |||
260 °C | 55 % Show Material materials with Dehnung of 55 % | T351 | Elongation in 50 mm | |||
315 °C | 75 % Show Material materials with Dehnung of 75 % | T351 | Elongation in 50 mm | |||
370 °C | 100 % Show Material materials with Dehnung of 100 % | T351 | Elongation in 50 mm | |||
Elastizitätsmodul | 72.4 GPa Show Material materials with Elastizitätsmodul of 72.4 GPa | T351 | ||||
73.0 GPa Show Material materials with Elastizitätsmodul of 73.0 GPa | T351 | AA Standards, ASTM B209, ASTM B211 | Bar | |||
73 GPa Show Material materials with Elastizitätsmodul of 73 GPa | T351 | |||||
Plane-Strain Fracture Toughnes | 26 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 26 MPa·√m | T351 | For plate in T-L direction | |||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | T351 | ||||
Schubmodule | 28.0 GPa Show Material materials with Schubmodule of 28.0 GPa | T351 | ||||
Streckgrenze | -80 °C | 338 MPa Show Material materials with Streckgrenze of 338 MPa | T351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
285.0 MPa Show Material materials with Streckgrenze of 285.0 MPa | T351 | AA Standards, ASTM B209 | RP02 | |||
290.0 MPa Show Material materials with Streckgrenze of 290.0 MPa | T351 | AA Standards, ASTM B209 | RP02 | |||
310.0 MPa Show Material materials with Streckgrenze of 310.0 MPa | T351 | AA Standards, ASTM B211 | Bar | RP02 | ||
0 °C | 324 MPa Show Material materials with Streckgrenze of 324 MPa | T351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
325.0 MPa Show Material materials with Streckgrenze of 325.0 MPa | T351 | |||||
330.0 MPa Show Material materials with Streckgrenze of 330.0 MPa | T351 | |||||
24 °C | 324 MPa Show Material materials with Streckgrenze of 324 MPa | T351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
100 °C | 310 MPa Show Material materials with Streckgrenze of 310 MPa | T351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
150 °C | 248 MPa Show Material materials with Streckgrenze of 248 MPa | T351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
205 °C | 131 MPa Show Material materials with Streckgrenze of 131 MPa | T351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
260 °C | 62 MPa Show Material materials with Streckgrenze of 62 MPa | T351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
315 °C | 41 MPa Show Material materials with Streckgrenze of 41 MPa | T351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
370 °C | 28 MPa Show Material materials with Streckgrenze of 28 MPa | T351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
Zugfestigkeit | -195 °C | 580 MPa Show Material materials with Zugfestigkeit of 580 MPa | T351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
-80 °C | 490 MPa Show Material materials with Zugfestigkeit of 490 MPa | T351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
395.0 MPa Show Material materials with Zugfestigkeit of 395.0 MPa | T351 | AA Standards, ASTM B209 | ||||
415.0 MPa Show Material materials with Zugfestigkeit of 415.0 MPa | T351 | AA Standards, ASTM B209 | ||||
425.0 MPa Show Material materials with Zugfestigkeit of 425.0 MPa | T351 | AA Standards, ASTM B209, ASTM B211 | ||||
427.0 MPa Show Material materials with Zugfestigkeit of 427.0 MPa | T351 | Bar | ||||
435.0 MPa Show Material materials with Zugfestigkeit of 435.0 MPa | T351 | AA Standards, ASTM B209 | ||||
440.0 MPa Show Material materials with Zugfestigkeit of 440.0 MPa | T351 | AA Standards, ASTM B209 | ||||
470.0 MPa Show Material materials with Zugfestigkeit of 470.0 MPa | T351 | |||||
0 °C | 475 MPa Show Material materials with Zugfestigkeit of 475 MPa | T351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
24 °C | 470 MPa Show Material materials with Zugfestigkeit of 470 MPa | T351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
100 °C | 435 MPa Show Material materials with Zugfestigkeit of 435 MPa | T351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
150 °C | 310 MPa Show Material materials with Zugfestigkeit of 310 MPa | T351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
205 °C | 180 MPa Show Material materials with Zugfestigkeit of 180 MPa | T351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
260 °C | 75 MPa Show Material materials with Zugfestigkeit of 75 MPa | T351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
315 °C | 52 MPa Show Material materials with Zugfestigkeit of 52 MPa | T351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
370 °C | 35 MPa Show Material materials with Zugfestigkeit of 35 MPa | T351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture |
Thermisch
| Property | Temperature | Value | Condition | Shape | Related Standards |
|---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 2.29e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.29e-05 1/K | T351 | |||
2.3e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3e-05 1/K | T351 | ||||
2.31e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.31e-05 1/K | T351 | Bar | |||
20 °C | 2.3199999999999998e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3199999999999998e-05 1/K | T351 | AA Standards, ASTM B209, ASTM B211 | ||
100 °C | 2.3199999999999998e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3199999999999998e-05 1/K | T351 | AA Standards, ASTM B209, ASTM B211 | ||
Schmelzpunkt | 500.0 °C Show Material materials with Schmelzpunkt of 500.0 °C | T351 | |||
505.0 - 635.0 °C Show Material materials with Schmelzpunkt of 505.0 - 635.0 °C | T351 | AA Standards, ASTM B209, ASTM B211 | |||
640.0 °C Show Material materials with Schmelzpunkt of 640.0 °C | T351 | Bar | |||
Spezifische Wärmekapazität | 870.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 870.0 J/(kg·K) | T351 | |||
875.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 875.0 J/(kg·K) | T351 | ||||
Wärmeleitfähigkeit | 120.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 120.0 W/(m·K) | T351 | |||
121.0 - 193.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 121.0 - 193.0 W/(m·K) | T351 | AA Standards, ASTM B209, ASTM B211 | |||
121.0 - 150.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 121.0 - 150.0 W/(m·K) | T351 | Bar |
Elektrisch
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Elektrische Leitfähigkeit | 17000000.0 - 29000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 17000000.0 - 29000000.0 S/m | T351 | AA Standards, ASTM B209, ASTM B211 | ||
spezifischer Widerstand | 3.45e-08 - 5.88e-08 Ω·m Show Material materials with spezifischer Widerstand of 3.45e-08 - 5.88e-08 Ω·m | T351 | AA Standards, ASTM B209, ASTM B211 | ||
4.31e-08 - 5.75e-08 Ω·m Show Material materials with spezifischer Widerstand of 4.31e-08 - 5.75e-08 Ω·m | T351 | Bar | |||
5.7e-08 Ω·m Show Material materials with spezifischer Widerstand of 5.7e-08 Ω·m | T351 | Typical value |
Chemical properties
| Property | Value | Condition | Shape | Related Standards | Comment |
|---|---|---|---|---|---|
Aluminium | 90.7 - 94.7 % Show Material materials with Aluminium of 90.7 - 94.7 % | T351 | |||
Andere | 0.15 % Show Material materials with Andere of 0.15 % | T351 | Bar | Total | |
Chrom | 0.1 % Show Material materials with Chrom of 0.1 % | T351 | Bar | AA Standards, ASTM B209, ASTM B211 | |
Eisen | 0.50 % Show Material materials with Eisen of 0.50 % | T351 | AA Standards, ASTM B209, ASTM B211 | ||
0.5 % Show Material materials with Eisen of 0.5 % | T351 | Bar | |||
Kupfer | 3.8 - 4.9 % Show Material materials with Kupfer of 3.8 - 4.9 % | T351 | Bar | AA Standards, ASTM B209, ASTM B211 | |
Magnesium | 1.2 - 1.8 % Show Material materials with Magnesium of 1.2 - 1.8 % | T351 | Bar | AA Standards, ASTM B209, ASTM B211 | |
Mangan | 0.3 - 0.9 % Show Material materials with Mangan of 0.3 - 0.9 % | T351 | Bar | AA Standards, ASTM B209, ASTM B211 | |
Silizium | 0.5 % Show Material materials with Silizium of 0.5 % | T351 | Bar | AA Standards, ASTM B209, ASTM B211 | |
Titan | 0.15 % Show Material materials with Titan of 0.15 % | T351 | Bar | AA Standards, ASTM B209, ASTM B211 | |
Zink | 0.25 % Show Material materials with Zink of 0.25 % | T351 | Bar | AA Standards, ASTM B209, ASTM B211 | |
Zirkonium | 0.2 % Show Material materials with Zirkonium of 0.2 % | T351 | Bar | Ti + Zr |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Aerospace | |
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: Betriebsschäden in Gebieten mit Zugspannungen quer zur Kornstruktur, Eingeschränkte Schäden an Laborproben (T4,T3, T351, T3510, T3511), d (T6, T861, T81, T851, T8510, T8511), general: sufficient, in principle it should be protected | |
| General machinability | General: poor (O), good to acceptable | |
| Workability | general (condition): poor(T4, T3, T351, T3510, T3511, T6), not suitable (T361, T861, T81, T851, T8510, T8511) | |