Aluminum AA 2024, known for its use in aircraft industry, is an alloy that offers excellent strength. When in the annealed condition it is readily formed and has good machinability. Though it has a relatively low level of corrosion resistance, it can be machined to a high finish.

Equivalent Materials

Diese Materialdaten wurden von MakeItFrom.com,ASM Handbook Volume 2 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials zur Verfügung gestellt

Alle Daten beziehen sich auf Raumtemperatur soweit nicht anderweitig spezifiziert. SI Einheiten werden verwendt soweit nicht anderweitig spezifiziert.
Äquivalente Standards sind ähnlich zu einem oder mehreren Standards die der Anbieter angegeben hat. Manche äquivalente Standards können strikter sein oder außerhalb der Bedingungen des ursprünglichen Standards.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Eigenschaften

Allgemein

PropertyValueCondition

Dichte

2.78 g/cm³

Show Material materials with Dichte of 2.78 g/cm³

T651

3.0 g/cm³

Show Material materials with Dichte of 3.0 g/cm³

T651

Mechanisch

PropertyTemperatureValueConditionComment

Dehnung

-195 °C

11 %

Show Material materials with Dehnung of 11 %

T651

Elongation in 50 mm

-80 °C

10 %

Show Material materials with Dehnung of 10 %

T651

Elongation in 50 mm

4.6 %

Show Material materials with Dehnung of 4.6 %

T651

0 °C

10 %

Show Material materials with Dehnung of 10 %

T651

Elongation in 50 mm

24 °C

10 %

Show Material materials with Dehnung of 10 %

T651

Elongation in 50 mm

100 °C

10 %

Show Material materials with Dehnung of 10 %

T651

Elongation in 50 mm

150 °C

17 %

Show Material materials with Dehnung of 17 %

T651

Elongation in 50 mm

205 °C

27 %

Show Material materials with Dehnung of 27 %

T651

Elongation in 50 mm

260 °C

55 %

Show Material materials with Dehnung of 55 %

T651

Elongation in 50 mm

315 °C

75 %

Show Material materials with Dehnung of 75 %

T651

Elongation in 50 mm

370 °C

100 %

Show Material materials with Dehnung of 100 %

T651

Elongation in 50 mm

Elastizitätsmodul

73.0 GPa

Show Material materials with Elastizitätsmodul of 73.0 GPa

T651

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m

Typical for Wrought 2000 Series Aluminium

Poissonzahl

0.33 [-]

Show Material materials with Poissonzahl of 0.33 [-]

Typical for Wrought 2000 Series Aluminium

Schubmodule

28.0 GPa

Show Material materials with Schubmodule of 28.0 GPa

T651

Streckgrenze

-195 °C

469 MPa

Show Material materials with Streckgrenze of 469 MPa

T651

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

-80 °C

407 MPa

Show Material materials with Streckgrenze of 407 MPa

T651

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

360.0 MPa

Show Material materials with Streckgrenze of 360.0 MPa

T651

0 °C

400 MPa

Show Material materials with Streckgrenze of 400 MPa

T651

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

24 °C

393 MPa

Show Material materials with Streckgrenze of 393 MPa

T651

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

100 °C

372 MPa

Show Material materials with Streckgrenze of 372 MPa

T651

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

150 °C

248 MPa

Show Material materials with Streckgrenze of 248 MPa

T651

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

205 °C

131 MPa

Show Material materials with Streckgrenze of 131 MPa

T651

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

260 °C

62 MPa

Show Material materials with Streckgrenze of 62 MPa

T651

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

315 °C

41 MPa

Show Material materials with Streckgrenze of 41 MPa

T651

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

370 °C

28 MPa

Show Material materials with Streckgrenze of 28 MPa

T651

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

Zugfestigkeit

-195 °C

580 MPa

Show Material materials with Zugfestigkeit of 580 MPa

T651

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

-80 °C

495 MPa

Show Material materials with Zugfestigkeit of 495 MPa

T651

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

0 °C

483 MPa

Show Material materials with Zugfestigkeit of 483 MPa

T651

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

490.0 MPa

Show Material materials with Zugfestigkeit of 490.0 MPa

T651

24 °C

475 MPa

Show Material materials with Zugfestigkeit of 475 MPa

T651

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

100 °C

448 MPa

Show Material materials with Zugfestigkeit of 448 MPa

T651

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

150 °C

310 MPa

Show Material materials with Zugfestigkeit of 310 MPa

T651

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

205 °C

180 MPa

Show Material materials with Zugfestigkeit of 180 MPa

T651

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

260 °C

75 MPa

Show Material materials with Zugfestigkeit of 75 MPa

T651

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

315 °C

52 MPa

Show Material materials with Zugfestigkeit of 52 MPa

T651

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

370 °C

35 MPa

Show Material materials with Zugfestigkeit of 35 MPa

T651

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

Thermisch

PropertyValueCondition

Koeffizient der thermischen Ausdehnung

2.3e-05 1/K

Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3e-05 1/K

T651

Schmelzpunkt

500.0 °C

Show Material materials with Schmelzpunkt of 500.0 °C

T651

Spezifische Wärmekapazität

870.0 J/(kg·K)

Show Material materials with Spezifische Wärmekapazität of 870.0 J/(kg·K)

T651

Wärmeleitfähigkeit

120.0 W/(m·K)

Show Material materials with Wärmeleitfähigkeit of 120.0 W/(m·K)

T651

Elektrisch

PropertyValueComment

Elektrische Leitfähigkeit

18000000.0 - 30000000.0 S/m

Show Material materials with Elektrische Leitfähigkeit of 18000000.0 - 30000000.0 S/m

Typical for Wrought 2000 Series Aluminium

spezifischer Widerstand

3.4e-08 - 6e-08 Ω·m

Show Material materials with spezifischer Widerstand of 3.4e-08 - 6e-08 Ω·m

Typical for Wrought 2000 Series Aluminium

Chemical properties

PropertyValueCondition

Aluminium

90.7 - 94.7 %

Show Material materials with Aluminium of 90.7 - 94.7 %

T651

Andere

0.15 %

Show Material materials with Andere of 0.15 %

T651

Chrom

0.1 %

Show Material materials with Chrom of 0.1 %

T651

Eisen

0.5 %

Show Material materials with Eisen of 0.5 %

T651

Kupfer

3.8 - 4.9 %

Show Material materials with Kupfer of 3.8 - 4.9 %

T651

Magnesium

1.2 - 1.8 %

Show Material materials with Magnesium of 1.2 - 1.8 %

T651

Mangan

0.3 - 0.9 %

Show Material materials with Mangan of 0.3 - 0.9 %

T651

Silizium

0.5 %

Show Material materials with Silizium of 0.5 %

T651

Titan

0.15 %

Show Material materials with Titan of 0.15 %

T651

Zink

0.25 %

Show Material materials with Zink of 0.25 %

T651

Zirkonium

0.2 %

Show Material materials with Zirkonium of 0.2 %

T651

Technological properties

Property
Workability

Moderate Workability

Looking for suppliers of this material? Click to see 124 supplier of AA 2024 T651 on Matmatch