Eigenschaften
Allgemein
| Property | Temperature | Value |
|---|---|---|
Dichte | 23.0 °C | 8.83 - 8.9 g/cm³ Show Material materials with Dichte of 8.83 - 8.9 g/cm³ |
Abmessung
| Property | Value | Comment | |
|---|---|---|---|
Außendurchmesser | 0.76 - 76 mm Show Material materials with Außendurchmesser of 0.76 - 76 mm | Rod | |
Breite | 305 - 559 mm Show Material materials with Breite of 305 - 559 mm | ||
Dicke | 0.76 - 76 mm Show Material materials with Dicke of 0.76 - 76 mm | max.,Bar | |
Durchmesser | 1.27 - 12.7 mm Show Material materials with Durchmesser of 1.27 - 12.7 mm | ||
Länge | 610 - 91000 mm Show Material materials with Länge of 610 - 91000 mm | max. Rod and Bar | |
Wall thickness | Typically 10 to 20% of OD | ||
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dehnung | 20.0 °C | 15 % Show Material materials with Dehnung of 15 % | min. |
23.0 °C | 5 - 25 % Show Material materials with Dehnung of 5 - 25 % | min. | |
427.0 °C | 5 % Show Material materials with Dehnung of 5 % | min. | |
Elastizitätsmodul | 23.0 °C | 138 - 140 GPa Show Material materials with Elastizitätsmodul of 138 - 140 GPa | |
Härte, Rockwell B | 23.0 °C | 92 [-] Show Material materials with Härte, Rockwell B of 92 [-] | |
Streckgrenze | 23.0 °C | 760 MPa Show Material materials with Streckgrenze of 760 MPa | |
Streckgrenze Rp 0,2 | 20.0 °C | 585 MPa Show Material materials with Streckgrenze Rp 0,2 of 585 MPa | |
23.0 °C | 650 - 870 MPa Show Material materials with Streckgrenze Rp 0,2 of 650 - 870 MPa | ||
427.0 °C | 450 MPa Show Material materials with Streckgrenze Rp 0,2 of 450 MPa | ||
Zugfestigkeit | 20.0 °C | 690 MPa Show Material materials with Zugfestigkeit of 690 MPa | |
23.0 °C | 750 - 970 MPa Show Material materials with Zugfestigkeit of 750 - 970 MPa | ||
427.0 °C | 515 MPa Show Material materials with Zugfestigkeit of 515 MPa | ||
Thermisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.76E-5 - 1.8E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.76E-5 - 1.8E-5 1/K | |
Schmelzpunkt | 1010 - 1020 °C Show Material materials with Schmelzpunkt of 1010 - 1020 °C | ||
Spezifische Wärmekapazität | 23.0 °C | 340 - 414 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 340 - 414 J/(kg·K) | at 25°C |
Wärmeleitfähigkeit | 23.0 °C | 200 - 225 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 200 - 225 W/(m·K) | at 25°C |
Elektrisch
| Property | Temperature | Value |
|---|---|---|
Specific Electrical conductivity | 45 - 60 % IACS Show Material materials with Specific Electrical conductivity of 45 - 60 % IACS | |
spezifischer Widerstand | 23.0 °C | 2.6E-6 - 3.8E-6 Ω·m Show Material materials with spezifischer Widerstand of 2.6E-6 - 3.8E-6 Ω·m |
Chemical properties
| Property | Value | Comment |
|---|---|---|
Aluminium | 0 - 0.2 % Show Material materials with Aluminium of 0 - 0.2 % | |
Andere | 0 - 0.5 % Show Material materials with Andere of 0 - 0.5 % | |
Beryllium | 0.4 - 0.7 % Show Material materials with Beryllium of 0.4 - 0.7 % | |
Eisen | 0 - 0.1 % Show Material materials with Eisen of 0 - 0.1 % | |
Kobalt | 2 - 2.7 % Show Material materials with Kobalt of 2 - 2.7 % | |
Kupfer | 95.6 - 97.2 % Show Material materials with Kupfer of 95.6 - 97.2 % | Balance |
Silizium | 0 - 0.2 % Show Material materials with Silizium of 0 - 0.2 % | |
Zirkonium | 0.12 - 0.4 % Show Material materials with Zirkonium of 0.12 - 0.4 % |
Technological properties
| Property | ||
|---|---|---|
| Application areas | High performance powertrain automotive applications such as exhaust valve seats.,Typical applications include resistance welding components, and inserts for metal die casting, injection molding and blow molding.,Typical applications include dies casting plunger tips and dies for steel extrusion.,Typical applications include heat exchanger tubing and resistance welding components.,Typical applications include coil springs and formed wire contacts. | |