Eigenschaften
Allgemein
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Dichte | 2.84 g/cm³ Show Material materials with Dichte of 2.84 g/cm³ | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
2.84 g/cm³ Show Material materials with Dichte of 2.84 g/cm³ | T62 | ||
3.1 g/cm³ Show Material materials with Dichte of 3.1 g/cm³ | T62 |
Mechanisch
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 105.0 MPa Show Material materials with Bending Fatigue Strength of 105.0 MPa | T62 | AA Standards | ||
Dehnung | -195 °C | 16 % Show Material materials with Dehnung of 16 % | T62 | Elongation in 50 mm | |
-80 °C | 13 % Show Material materials with Dehnung of 13 % | T62 | Elongation in 50 mm | ||
5.0 % Show Material materials with Dehnung of 5.0 % | T62 | AA Standards, ASTM B221, ASTM B241 | A100 | ||
6.0 % Show Material materials with Dehnung of 6.0 % | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | A50 | ||
6.0 % Show Material materials with Dehnung of 6.0 % | T62 | AA Standards, ASTM B209 | A100 | ||
7.0 % Show Material materials with Dehnung of 7.0 % | T62 | AA Standards, ASTM B209 | A50 | ||
7.0 % Show Material materials with Dehnung of 7.0 % | T62 | AA Standards, ASTM B209 | A100 | ||
8.0 % Show Material materials with Dehnung of 8.0 % | T62 | AA Standards, ASTM B209 | A50 | ||
8.2 % Show Material materials with Dehnung of 8.2 % | T62 | ||||
10.0 % Show Material materials with Dehnung of 10.0 % | T62 | AA Standards | A50 | ||
0 °C | 12 % Show Material materials with Dehnung of 12 % | T62 | Elongation in 50 mm | ||
24 °C | 12 % Show Material materials with Dehnung of 12 % | T62 | Elongation in 50 mm | ||
100 °C | 14 % Show Material materials with Dehnung of 14 % | T62 | Elongation in 50 mm | ||
150 °C | 17 % Show Material materials with Dehnung of 17 % | T62 | Elongation in 50 mm | ||
205 °C | 20 % Show Material materials with Dehnung of 20 % | T62 | Elongation in 50 mm | ||
260 °C | 21 % Show Material materials with Dehnung of 21 % | T62 | Elongation in 50 mm | ||
315 °C | 40 % Show Material materials with Dehnung of 40 % | T62 | Elongation in 50 mm | ||
370 °C | 75 % Show Material materials with Dehnung of 75 % | T62 | Elongation in 50 mm | ||
Elastizitätsmodul | 73.0 GPa Show Material materials with Elastizitätsmodul of 73.0 GPa | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | ||
73 GPa Show Material materials with Elastizitätsmodul of 73 GPa | T62 | ||||
74.0 GPa Show Material materials with Elastizitätsmodul of 74.0 GPa | T62 | ||||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | |||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | |||
Schubmodule | 26.0 GPa Show Material materials with Schubmodule of 26.0 GPa | T62 | |||
Streckgrenze | 250.0 MPa Show Material materials with Streckgrenze of 250.0 MPa | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | RP02 | |
290.0 MPa Show Material materials with Streckgrenze of 290.0 MPa | T62 | AA Standards | RP02 | ||
290.0 MPa Show Material materials with Streckgrenze of 290.0 MPa | T62 | ||||
Zugfestigkeit | -195 °C | 503 MPa Show Material materials with Zugfestigkeit of 503 MPa | T62 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 435 MPa Show Material materials with Zugfestigkeit of 435 MPa | T62 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370.0 MPa Show Material materials with Zugfestigkeit of 370.0 MPa | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | |||
415.0 MPa Show Material materials with Zugfestigkeit of 415.0 MPa | T62 | AA Standards | |||
0 °C | 415 MPa Show Material materials with Zugfestigkeit of 415 MPa | T62 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
420.0 MPa Show Material materials with Zugfestigkeit of 420.0 MPa | T62 | ||||
24 °C | 400 MPa Show Material materials with Zugfestigkeit of 400 MPa | T62 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 372 MPa Show Material materials with Zugfestigkeit of 372 MPa | T62 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 310 MPa Show Material materials with Zugfestigkeit of 310 MPa | T62 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 235 MPa Show Material materials with Zugfestigkeit of 235 MPa | T62 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 185 MPa Show Material materials with Zugfestigkeit of 185 MPa | T62 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 70 MPa Show Material materials with Zugfestigkeit of 70 MPa | T62 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 30 MPa Show Material materials with Zugfestigkeit of 30 MPa | T62 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture |
Thermisch
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 2.2e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.2e-05 1/K | T62 | ||
20 °C | 2.23e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.23e-05 1/K | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | |
100 °C | 2.23e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.23e-05 1/K | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | |
Schmelzpunkt | 540.0 °C Show Material materials with Schmelzpunkt of 540.0 °C | T62 | ||
545.0 - 645.0 °C Show Material materials with Schmelzpunkt of 545.0 - 645.0 °C | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | ||
Spezifische Wärmekapazität | 860.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 860.0 J/(kg·K) | T62 | ||
Wärmeleitfähigkeit | 113.0 - 172.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 113.0 - 172.0 W/(m·K) | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | |
140.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 140.0 W/(m·K) | T62 |
Elektrisch
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elektrische Leitfähigkeit | 16000000.0 - 26000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 16000000.0 - 26000000.0 S/m | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | |
17000000 S/m Show Material materials with Elektrische Leitfähigkeit of 17000000 S/m | T62 | Typical/derived value | ||
Specific Electrical conductivity | 30.0 % IACS Show Material materials with Specific Electrical conductivity of 30.0 % IACS | T62 | Typical value | |
spezifischer Widerstand | 3.85e-08 - 6.25e-08 Ω·m Show Material materials with spezifischer Widerstand of 3.85e-08 - 6.25e-08 Ω·m | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | |
6.2e-08 Ω·m Show Material materials with spezifischer Widerstand of 6.2e-08 Ω·m | T62 | Typical value |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 91.5 - 93.8 % Show Material materials with Aluminium of 91.5 - 93.8 % | T62 | |
Andere | 0.15 % Show Material materials with Andere of 0.15 % | T62 | |
Eisen | 0.30 % Show Material materials with Eisen of 0.30 % | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
0.3 % Show Material materials with Eisen of 0.3 % | T62 | ||
Kupfer | 5.8 - 6.8 % Show Material materials with Kupfer of 5.8 - 6.8 % | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Magnesium | 0.02 % Show Material materials with Magnesium of 0.02 % | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Mangan | 0.2 - 0.4 % Show Material materials with Mangan of 0.2 - 0.4 % | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Silizium | 0.2 % Show Material materials with Silizium of 0.2 % | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Titan | 0.02 - 0.1 % Show Material materials with Titan of 0.02 - 0.1 % | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Vanadium | 0.05 - 0.15 % Show Material materials with Vanadium of 0.05 - 0.15 % | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Zink | 0.1 % Show Material materials with Zink of 0.1 % | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Zirkonium | 0.1 - 0.25 % Show Material materials with Zirkonium of 0.1 - 0.25 % | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: Betriebsschäden in Gebieten mit Zugspannungen quer zur Kornstruktur, Eingeschränkte Schäden an Laborproben (T31, T351, T3510, T3511, T37), kein Schadensfall im Betrieb, eingeschränkte Schäden bei den Labortests (T81, T851, T8510, T8511), general: sufficient, in principle it should be protected | |
| General machinability | General: good to acceptable | |
| Workability | general (condition): poor(T31, T351, T3510, T3511), not suitable (T37, T81, T851, T8510, T8511, T87) | |