Eigenschaften
Allgemein
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Dichte | 2.84 g/cm³ Show Material materials with Dichte of 2.84 g/cm³ | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
2.84 g/cm³ Show Material materials with Dichte of 2.84 g/cm³ | T81 | ||
3.1 g/cm³ Show Material materials with Dichte of 3.1 g/cm³ | T81 |
Mechanisch
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 105.0 MPa Show Material materials with Bending Fatigue Strength of 105.0 MPa | T81 | AA Standards | ||
Dehnung | 5.0 % Show Material materials with Dehnung of 5.0 % | T81 | AA Standards, ASTM B221, ASTM B241 | A100 | |
6.0 % Show Material materials with Dehnung of 6.0 % | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | A50 | ||
7.0 % Show Material materials with Dehnung of 7.0 % | T81 | AA Standards, ASTM B209 | A50 | ||
8.2 % Show Material materials with Dehnung of 8.2 % | T81 | ||||
10.0 % Show Material materials with Dehnung of 10.0 % | T81 | AA Standards | A50 | ||
10 % Show Material materials with Dehnung of 10 % | T81 | ||||
Elastizitätsmodul | 73.0 GPa Show Material materials with Elastizitätsmodul of 73.0 GPa | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | ||
73 GPa Show Material materials with Elastizitätsmodul of 73 GPa | T81 | ||||
74.0 GPa Show Material materials with Elastizitätsmodul of 74.0 GPa | T81 | ||||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | |||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | |||
Schubmodule | 26.0 GPa Show Material materials with Schubmodule of 26.0 GPa | T81 | |||
Streckgrenze | -196 °C | 421 MPa Show Material materials with Streckgrenze of 421 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
-80 °C | 372 MPa Show Material materials with Streckgrenze of 372 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-28 °C | 359 MPa Show Material materials with Streckgrenze of 359 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
290.0 MPa Show Material materials with Streckgrenze of 290.0 MPa | T81 | AA Standards, ASTM B221, ASTM B241 | RP02 | ||
315.0 MPa Show Material materials with Streckgrenze of 315.0 MPa | T81 | AA Standards, ASTM B209 | RP02 | ||
350.0 MPa Show Material materials with Streckgrenze of 350.0 MPa | T81 | AA Standards | RP02 | ||
350.0 MPa Show Material materials with Streckgrenze of 350.0 MPa | T81 | ||||
24 °C | 345 MPa Show Material materials with Streckgrenze of 345 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
100 °C | 324 MPa Show Material materials with Streckgrenze of 324 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
149 °C | 276 MPa Show Material materials with Streckgrenze of 276 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
204 °C | 200 MPa Show Material materials with Streckgrenze of 200 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
260 °C | 159 MPa Show Material materials with Streckgrenze of 159 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
316 °C | 41 MPa Show Material materials with Streckgrenze of 41 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
371 °C | 26 MPa Show Material materials with Streckgrenze of 26 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
Zugfestigkeit | -195 °C | 572 MPa Show Material materials with Zugfestigkeit of 572 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 490 MPa Show Material materials with Zugfestigkeit of 490 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
400.0 MPa Show Material materials with Zugfestigkeit of 400.0 MPa | T81 | AA Standards, ASTM B221, ASTM B241 | |||
425.0 MPa Show Material materials with Zugfestigkeit of 425.0 MPa | T81 | AA Standards, ASTM B209 | |||
455.0 MPa Show Material materials with Zugfestigkeit of 455.0 MPa | T81 | AA Standards | |||
470.0 MPa Show Material materials with Zugfestigkeit of 470.0 MPa | T81 | ||||
0 °C | 475 MPa Show Material materials with Zugfestigkeit of 475 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
24 °C | 455 MPa Show Material materials with Zugfestigkeit of 455 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 415 MPa Show Material materials with Zugfestigkeit of 415 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 338 MPa Show Material materials with Zugfestigkeit of 338 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 248 MPa Show Material materials with Zugfestigkeit of 248 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 200 MPa Show Material materials with Zugfestigkeit of 200 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 48 MPa Show Material materials with Zugfestigkeit of 48 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 30 MPa Show Material materials with Zugfestigkeit of 30 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture |
Thermisch
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 2.2e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.2e-05 1/K | T81 | ||
20 °C | 2.23e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.23e-05 1/K | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | |
100 °C | 2.23e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.23e-05 1/K | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | |
Schmelzpunkt | 540.0 °C Show Material materials with Schmelzpunkt of 540.0 °C | T81 | ||
545.0 - 645.0 °C Show Material materials with Schmelzpunkt of 545.0 - 645.0 °C | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | ||
Spezifische Wärmekapazität | 860.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 860.0 J/(kg·K) | T81 | ||
Wärmeleitfähigkeit | 113.0 - 172.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 113.0 - 172.0 W/(m·K) | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | |
120.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 120.0 W/(m·K) | T81 |
Elektrisch
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elektrische Leitfähigkeit | 16000000.0 - 26000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 16000000.0 - 26000000.0 S/m | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | |
17000000 S/m Show Material materials with Elektrische Leitfähigkeit of 17000000 S/m | T81 | Typical value | ||
Specific Electrical conductivity | 29.0 % IACS Show Material materials with Specific Electrical conductivity of 29.0 % IACS | T81 | Typical/Derived value | |
spezifischer Widerstand | 3.85e-08 - 6.25e-08 Ω·m Show Material materials with spezifischer Widerstand of 3.85e-08 - 6.25e-08 Ω·m | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | |
5.8e-08 Ω·m Show Material materials with spezifischer Widerstand of 5.8e-08 Ω·m | T81 | Typical value |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 91.5 - 93.8 % Show Material materials with Aluminium of 91.5 - 93.8 % | T81 | |
Andere | 0.15 % Show Material materials with Andere of 0.15 % | T81 | |
Eisen | 0.30 % Show Material materials with Eisen of 0.30 % | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
0.3 % Show Material materials with Eisen of 0.3 % | T81 | ||
Kupfer | 5.8 - 6.8 % Show Material materials with Kupfer of 5.8 - 6.8 % | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Magnesium | 0.02 % Show Material materials with Magnesium of 0.02 % | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Mangan | 0.2 - 0.4 % Show Material materials with Mangan of 0.2 - 0.4 % | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Silizium | 0.2 % Show Material materials with Silizium of 0.2 % | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Titan | 0.02 - 0.1 % Show Material materials with Titan of 0.02 - 0.1 % | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Vanadium | 0.05 - 0.15 % Show Material materials with Vanadium of 0.05 - 0.15 % | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Zink | 0.1 % Show Material materials with Zink of 0.1 % | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Zirkonium | 0.1 - 0.25 % Show Material materials with Zirkonium of 0.1 - 0.25 % | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: Betriebsschäden in Gebieten mit Zugspannungen quer zur Kornstruktur, Eingeschränkte Schäden an Laborproben (T31, T351, T3510, T3511, T37), kein Schadensfall im Betrieb, eingeschränkte Schäden bei den Labortests (T81, T851, T8510, T8511), general: sufficient, in principle it should be protected | |
| General machinability | General: good to acceptable | |
| Workability | general (condition): poor(T31, T351, T3510, T3511), not suitable (T37, T81, T851, T8510, T8511, T87) | |