Eigenschaften
Allgemein
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Dichte | 2.73 g/cm³ Show Material materials with Dichte of 2.73 g/cm³ | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
2.73 g/cm³ Show Material materials with Dichte of 2.73 g/cm³ | H14 | ||
2.8 g/cm³ Show Material materials with Dichte of 2.8 g/cm³ | H14 |
Mechanisch
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 60.0 MPa Show Material materials with Bending Fatigue Strength of 60.0 MPa | H14 | AA Standards | ||
Dauerfestigkeit | 62 MPa Show Material materials with Dauerfestigkeit of 62 MPa | H14 | for 5x10⁸ cycles | ||
Dehnung | -195 °C | 30 % Show Material materials with Dehnung of 30 % | H14 | Elongation in 50 mm | |
-80 °C | 18 % Show Material materials with Dehnung of 18 % | H14 | Elongation in 50 mm | ||
1.0 % Show Material materials with Dehnung of 1.0 % | H14 | AA Standards, ASTM B209 | A50 | ||
2.0 % Show Material materials with Dehnung of 2.0 % | H14 | AA Standards, ASTM B209 | A50 | ||
3.0 % Show Material materials with Dehnung of 3.0 % | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B234, ASTM B313 | A50 | ||
3.0 % Show Material materials with Dehnung of 3.0 % | H14 | AA Standards, ASTM B234 | A100 | ||
4.0 % Show Material materials with Dehnung of 4.0 % | H14 | AA Standards, ASTM B210 | A50 | ||
4.0 % Show Material materials with Dehnung of 4.0 % | H14 | AA Standards, ASTM B234 | A100 | ||
5.0 % Show Material materials with Dehnung of 5.0 % | H14 | AA Standards, ASTM B209, ASTM B234, ASTM B313, ASTM B547 | A50 | ||
7.0 % Show Material materials with Dehnung of 7.0 % | H14 | AA Standards, ASTM B209 | A100 | ||
7.5 % Show Material materials with Dehnung of 7.5 % | H14 | ||||
8.0 % Show Material materials with Dehnung of 8.0 % | H14 | AA Standards, ASTM B209, ASTM B234, ASTM B547 | A50 | ||
14.0 % Show Material materials with Dehnung of 14.0 % | H14 | AA Standards | A100 | ||
0 °C | 16 % Show Material materials with Dehnung of 16 % | H14 | Elongation in 50 mm | ||
24 °C | 16 % Show Material materials with Dehnung of 16 % | H14 | Elongation in 50 mm | ||
100 °C | 16 % Show Material materials with Dehnung of 16 % | H14 | Elongation in 50 mm | ||
150 °C | 16 % Show Material materials with Dehnung of 16 % | H14 | Elongation in 50 mm | ||
205 °C | 20 % Show Material materials with Dehnung of 20 % | H14 | Elongation in 50 mm | ||
260 °C | 60 % Show Material materials with Dehnung of 60 % | H14 | Elongation in 50 mm | ||
315 °C | 70 % Show Material materials with Dehnung of 70 % | H14 | Elongation in 50 mm | ||
370 °C | 70 % Show Material materials with Dehnung of 70 % | H14 | Elongation in 50 mm | ||
Elastizitätsmodul | 69.0 GPa Show Material materials with Elastizitätsmodul of 69.0 GPa | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | ||
69 GPa Show Material materials with Elastizitätsmodul of 69 GPa | H14 | ||||
Härte, Brinell | 40.0 [-] Show Material materials with Härte, Brinell of 40.0 [-] | H14 | AA Standards | ||
40.0 [-] Show Material materials with Härte, Brinell of 40.0 [-] | H14 | 500 kg load, 10 mm ball | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 3000 Series Aluminium | |||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 3000 Series Aluminium | |||
Scherfestigkeit | 97.0 MPa Show Material materials with Scherfestigkeit of 97.0 MPa | H14 | |||
Schubmodule | 25.0 GPa Show Material materials with Schubmodule of 25.0 GPa | H14 | |||
Streckgrenze | -200 °C | 170 MPa Show Material materials with Streckgrenze of 170 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
-100 °C | 155 MPa Show Material materials with Streckgrenze of 155 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-30 °C | 145 MPa Show Material materials with Streckgrenze of 145 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
115.0 MPa Show Material materials with Streckgrenze of 115.0 MPa | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B234, ASTM B313, ASTM B483, ASTM B547 | RP02 | ||
130.0 MPa Show Material materials with Streckgrenze of 130.0 MPa | H14 | ||||
145.0 MPa Show Material materials with Streckgrenze of 145.0 MPa | H14 | AA Standards | RP02 | ||
25 °C | 145 MPa Show Material materials with Streckgrenze of 145 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
100 °C | 130 MPa Show Material materials with Streckgrenze of 130 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
200 °C | 62 MPa Show Material materials with Streckgrenze of 62 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
300 °C | 17 MPa Show Material materials with Streckgrenze of 17 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
400 °C | 12 MPa Show Material materials with Streckgrenze of 12 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
Zugfestigkeit | -195 °C | 240 MPa Show Material materials with Zugfestigkeit of 240 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 165 MPa Show Material materials with Zugfestigkeit of 165 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
140.0 - 180.0 MPa Show Material materials with Zugfestigkeit of 140.0 - 180.0 MPa | H14 | AA Standards, ASTM B209, ASTM B313, ASTM B316, ASTM B547 | |||
140.0 MPa Show Material materials with Zugfestigkeit of 140.0 MPa | H14 | AA Standards, ASTM B210, ASTM B211, ASTM B234, ASTM B483 | |||
150.0 MPa Show Material materials with Zugfestigkeit of 150.0 MPa | H14 | AA Standards | |||
0 °C | 152 MPa Show Material materials with Zugfestigkeit of 152 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
160.0 MPa Show Material materials with Zugfestigkeit of 160.0 MPa | H14 | ||||
24 °C | 152 MPa Show Material materials with Zugfestigkeit of 152 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 145 MPa Show Material materials with Zugfestigkeit of 145 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 125 MPa Show Material materials with Zugfestigkeit of 125 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 97 MPa Show Material materials with Zugfestigkeit of 97 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 52 MPa Show Material materials with Zugfestigkeit of 52 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 28 MPa Show Material materials with Zugfestigkeit of 28 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 19 MPa Show Material materials with Zugfestigkeit of 19 MPa | H14 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture |
Thermisch
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 2.3e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3e-05 1/K | H14 | ||
20 °C | 2.3199999999999998e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3199999999999998e-05 1/K | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
100 °C | 2.3199999999999998e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3199999999999998e-05 1/K | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
Schmelzpunkt | 640.0 - 655.0 °C Show Material materials with Schmelzpunkt of 640.0 - 655.0 °C | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
640.0 °C Show Material materials with Schmelzpunkt of 640.0 °C | H14 | |||
Spezifische Wärmekapazität | 890.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 890.0 J/(kg·K) | H14 | ||
Wärmeleitfähigkeit | 159.0 - 193.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 159.0 - 193.0 W/(m·K) | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
180.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 180.0 W/(m·K) | H14 |
Elektrisch
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elektrische Leitfähigkeit | 24000000.0 - 29000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 24000000.0 - 29000000.0 S/m | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
24000000 S/m Show Material materials with Elektrische Leitfähigkeit of 24000000 S/m | H14 | Typical value | ||
Specific Electrical conductivity | 41.0 % IACS Show Material materials with Specific Electrical conductivity of 41.0 % IACS | H14 | Typical/Derived value | |
spezifischer Widerstand | 3.45e-08 - 4.17e-08 Ω·m Show Material materials with spezifischer Widerstand of 3.45e-08 - 4.17e-08 Ω·m | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
4.2e-08 Ω·m Show Material materials with spezifischer Widerstand of 4.2e-08 Ω·m | H14 | Typical value |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 96.8 - 99.0 % Show Material materials with Aluminium of 96.8 - 99.0 % | H14 | |
Andere | 0.15 % Show Material materials with Andere of 0.15 % | H14 | |
Eisen | 0.70 % Show Material materials with Eisen of 0.70 % | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
0.7 % Show Material materials with Eisen of 0.7 % | H14 | ||
Kupfer | 0.05 - 0.2 % Show Material materials with Kupfer of 0.05 - 0.2 % | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Mangan | 1.0 - 1.5 % Show Material materials with Mangan of 1.0 - 1.5 % | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Silizium | 0.6 % Show Material materials with Silizium of 0.6 % | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Zink | 0.1 % Show Material materials with Zink of 0.1 % | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: possible with commercial processes and methods | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: not suitable (O, H12), poor (H14, H16, H25) | |
| Workability | general (condition): good (O, H12), acceptable (H14, H25), poor(H16, H18) | |