Eigenschaften
Allgemein
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Dichte | 2.73 g/cm³ Show Material materials with Dichte of 2.73 g/cm³ | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547, BS EN 573-3, BS EN 485-2 | Sheet |
2.73 g/cm³ Show Material materials with Dichte of 2.73 g/cm³ | O | |||
2.8 g/cm³ Show Material materials with Dichte of 2.8 g/cm³ | O |
Mechanisch
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Bending Fatigue Strength | 50.0 MPa Show Material materials with Bending Fatigue Strength of 50.0 MPa | O | AA Standards | |||
Dauerfestigkeit | 48 MPa Show Material materials with Dauerfestigkeit of 48 MPa | O | for 5x10⁸ cycles | |||
Dehnung | -195 °C | 46 % Show Material materials with Dehnung of 46 % | O | Elongation in 50 mm | ||
-80 °C | 42 % Show Material materials with Dehnung of 42 % | O | Elongation in 50 mm | |||
14.0 % Show Material materials with Dehnung of 14.0 % | O | AA Standards, ASTM B209 | A50 | |||
20.0 % Show Material materials with Dehnung of 20.0 % | O | AA Standards, ASTM B209, ASTM B210 | A50 | |||
21.0 % Show Material materials with Dehnung of 21.0 % | O | AA Standards, ASTM B209 | A100 | |||
22.0 % Show Material materials with Dehnung of 22.0 % | O | AA Standards, ASTM B209, ASTM B313 | A50 | |||
22.0 % Show Material materials with Dehnung of 22.0 % | O | AA Standards, ASTM B211, ASTM B221, ASTM B241, ASTM B345 | A100 | |||
23.0 % Show Material materials with Dehnung of 23.0 % | O | AA Standards, ASTM B209, ASTM B547 | A50 | |||
25.0 % Show Material materials with Dehnung of 25.0 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 | A50 | |||
27.0 % Show Material materials with Dehnung of 27.0 % | O | AA Standards, ASTM B210 | A100 | |||
27.0 % Show Material materials with Dehnung of 27.0 % | O | |||||
30.0 % Show Material materials with Dehnung of 30.0 % | O | AA Standards, ASTM B210 | A50 | |||
37.0 % Show Material materials with Dehnung of 37.0 % | O | AA Standards | A100 | |||
0 °C | 41 % Show Material materials with Dehnung of 41 % | O | Elongation in 50 mm | |||
24 °C | 40 % Show Material materials with Dehnung of 40 % | O | Elongation in 50 mm | |||
100 °C | 43 % Show Material materials with Dehnung of 43 % | O | Elongation in 50 mm | |||
150 °C | 47 % Show Material materials with Dehnung of 47 % | O | Elongation in 50 mm | |||
205 °C | 60 % Show Material materials with Dehnung of 60 % | O | Elongation in 50 mm | |||
260 °C | 65 % Show Material materials with Dehnung of 65 % | O | Elongation in 50 mm | |||
315 °C | 70 % Show Material materials with Dehnung of 70 % | O | Elongation in 50 mm | |||
370 °C | 70 % Show Material materials with Dehnung of 70 % | O | Elongation in 50 mm | |||
Elastizitätsmodul | 69.0 GPa Show Material materials with Elastizitätsmodul of 69.0 GPa | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 | |||
69 GPa Show Material materials with Elastizitätsmodul of 69 GPa | O | |||||
69.5 GPa Show Material materials with Elastizitätsmodul of 69.5 GPa | O | BS EN 573-3, BS EN 485-2 | Sheet | |||
Härte, Brinell | 28.0 [-] Show Material materials with Härte, Brinell of 28.0 [-] | O | AA Standards, BS EN 573-3, BS EN 485-2 | Sheet | ||
28.0 [-] Show Material materials with Härte, Brinell of 28.0 [-] | O | 500 kg load, 10 mm ball | ||||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 3000 Series Aluminium | ||||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 3000 Series Aluminium | ||||
Scherfestigkeit | 76.0 MPa Show Material materials with Scherfestigkeit of 76.0 MPa | O | ||||
Schubmodule | 25.0 GPa Show Material materials with Schubmodule of 25.0 GPa | O | ||||
Streckgrenze | -200 °C | 60 MPa Show Material materials with Streckgrenze of 60 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-100 °C | 52 MPa Show Material materials with Streckgrenze of 52 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
-30 °C | 45 MPa Show Material materials with Streckgrenze of 45 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
35.0 MPa Show Material materials with Streckgrenze of 35.0 MPa | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547, BS EN 573-3, BS EN 485-2 | Sheet | RP02 | ||
40.0 MPa Show Material materials with Streckgrenze of 40.0 MPa | O | AA Standards | RP02 | |||
40.0 MPa Show Material materials with Streckgrenze of 40.0 MPa | O | |||||
25 °C | 41 MPa Show Material materials with Streckgrenze of 41 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
100 °C | 38 MPa Show Material materials with Streckgrenze of 38 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
200 °C | 30 MPa Show Material materials with Streckgrenze of 30 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
300 °C | 17 MPa Show Material materials with Streckgrenze of 17 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
400 °C | 12 MPa Show Material materials with Streckgrenze of 12 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
Zugfestigkeit | -195 °C | 228 MPa Show Material materials with Zugfestigkeit of 228 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
-80 °C | 138 MPa Show Material materials with Zugfestigkeit of 138 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
95.0 - 130.0 MPa Show Material materials with Zugfestigkeit of 95.0 - 130.0 MPa | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 | ||||
95.0 MPa Show Material materials with Zugfestigkeit of 95.0 MPa | O | AA Standards, ASTM B210, ASTM B483 | ||||
95.0 - 135.0 MPa Show Material materials with Zugfestigkeit of 95.0 - 135.0 MPa | O | BS EN 573-3, BS EN 485-2 | Sheet | |||
110.0 MPa Show Material materials with Zugfestigkeit of 110.0 MPa | O | AA Standards | ||||
0 °C | 117 MPa Show Material materials with Zugfestigkeit of 117 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
130.0 - 135.0 MPa Show Material materials with Zugfestigkeit of 130.0 - 135.0 MPa | O | AA Standards, ASTM B316 | ||||
24 °C | 110 MPa Show Material materials with Zugfestigkeit of 110 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
100 °C | 90 MPa Show Material materials with Zugfestigkeit of 90 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
150 °C | 75 MPa Show Material materials with Zugfestigkeit of 75 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
205 °C | 59 MPa Show Material materials with Zugfestigkeit of 59 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
260 °C | 40 MPa Show Material materials with Zugfestigkeit of 40 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
315 °C | 28 MPa Show Material materials with Zugfestigkeit of 28 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
370 °C | 19 MPa Show Material materials with Zugfestigkeit of 19 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture |
Thermisch
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 2.3e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3e-05 1/K | O | |||
2.31e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.31e-05 1/K | O | BS EN 573-3, BS EN 485-2 | Sheet | ||
20 °C | 2.3199999999999998e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3199999999999998e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 | ||
100 °C | 2.3199999999999998e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3199999999999998e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 | ||
Schmelzpunkt | 640.0 - 655.0 °C Show Material materials with Schmelzpunkt of 640.0 - 655.0 °C | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 | ||
640.0 °C Show Material materials with Schmelzpunkt of 640.0 °C | O | ||||
655.0 °C Show Material materials with Schmelzpunkt of 655.0 °C | O | BS EN 573-3, BS EN 485-2 | Sheet | ||
Spezifische Wärmekapazität | 890.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 890.0 J/(kg·K) | O | |||
Wärmeleitfähigkeit | 159.0 - 193.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 159.0 - 193.0 W/(m·K) | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 | ||
180.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 180.0 W/(m·K) | O | ||||
190.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 190.0 W/(m·K) | O | BS EN 573-3, BS EN 485-2 | Sheet |
Elektrisch
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Elektrische Leitfähigkeit | 24000000.0 - 29000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 24000000.0 - 29000000.0 S/m | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 | ||
29000000 S/m Show Material materials with Elektrische Leitfähigkeit of 29000000 S/m | O | Typical/derived value | |||
Specific Electrical conductivity | 50.0 % IACS Show Material materials with Specific Electrical conductivity of 50.0 % IACS | O | Typical value | ||
spezifischer Widerstand | 3.4e-08 Ω·m Show Material materials with spezifischer Widerstand of 3.4e-08 Ω·m | O | BS EN 573-3, BS EN 485-2 | Sheet | |
3.45e-08 - 4.17e-08 Ω·m Show Material materials with spezifischer Widerstand of 3.45e-08 - 4.17e-08 Ω·m | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 | |||
3.5e-08 Ω·m Show Material materials with spezifischer Widerstand of 3.5e-08 Ω·m | O | Typical value |
Chemical properties
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Aluminium | 96.8 - 99.0 % Show Material materials with Aluminium of 96.8 - 99.0 % | O | |||
Andere | 0.05 % Show Material materials with Andere of 0.05 % | O | BS EN 573-3, BS EN 485-2 | Sheet | Total |
0.15 % Show Material materials with Andere of 0.15 % | O | ||||
Eisen | 0.6 % Show Material materials with Eisen of 0.6 % | O | BS EN 573-3, BS EN 485-2 | Sheet | Si + Fe |
0.70 % Show Material materials with Eisen of 0.70 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 | |||
0.7 % Show Material materials with Eisen of 0.7 % | O | ||||
Kobalt | 0.05 - 0.2 % Show Material materials with Kobalt of 0.05 - 0.2 % | O | BS EN 573-3, BS EN 485-2 | Sheet | |
Kupfer | 0.05 - 0.2 % Show Material materials with Kupfer of 0.05 - 0.2 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 | ||
Magnesium | 1.0 - 1.5 % Show Material materials with Magnesium of 1.0 - 1.5 % | O | BS EN 573-3, BS EN 485-2 | Sheet | |
Mangan | 1.0 - 1.5 % Show Material materials with Mangan of 1.0 - 1.5 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 | ||
Silizium | 0.6 % Show Material materials with Silizium of 0.6 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547, BS EN 573-3, BS EN 485-2 | Sheet | Si + Fe |
Wasserstoff | 0.7 Show Material materials with Wasserstoff of 0.7 | O | BS EN 573-3, BS EN 485-2 | Sheet | |
Zink | 0.1 % Show Material materials with Zink of 0.1 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 | ||
Zirkonium | 0.1 % Show Material materials with Zirkonium of 0.1 % | O | BS EN 573-3, BS EN 485-2 | Sheet |
Technological properties
| Property | ||
|---|---|---|
| Application areas | roofing and sidings, acoustic ceilings, corrugated sheets, storage tanks, pipes, metal work, heat exchangers, air condition evaporators, motor vehicle radiators, freezer linings, cooking utensils, bakery moulds, office equipment, tubes & pipes, containers, closures, cladding alloymetal workcorrugated sheets, | |
| Brazing | general: possible with commercial processes and methods | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: not suitable (O, H12), poor (H14, H16, H25) | |
| Soldering general | Very Good | |
| Welding | Gas: Very Good; Arc: Very Good; Resistance: Good | |
| Workability | general (condition): good (O, H12), acceptable (H14, H25), poor(H16, H18) | |