AA Standards Grade 3004 H34

Want to keep this datasheet? Save it now in your required format

Related Standards

Equivalent Materials

Diese Materialdaten wurden von AluKey,MakeItFrom.com,ASM Handbook Volume 2 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials zur Verfügung gestellt

Alle Daten beziehen sich auf Raumtemperatur soweit nicht anderweitig spezifiziert. SI Einheiten werden verwendt soweit nicht anderweitig spezifiziert.
Äquivalente Standards sind ähnlich zu einem oder mehreren Standards die der Anbieter angegeben hat. Manche äquivalente Standards können strikter sein oder außerhalb der Bedingungen des ursprünglichen Standards.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Suppliers with similar grades

ALUDIUM

HERSTELLER

Information and services

Quantity:

One truck load – Specialty products on request.

Additional services:

Via Cindal (the Aludium R&D department): R&D services, benchmarking, chemical audits, material specification, process optimisation, quality monitoring, sample analysis, prototyping, training

AMS METAL LOGO

PROCESSOR AND DISTRIBUTOR

AA METALS INC.

PROCESSOR AND DISTRIBUTOR

There are 20 other suppliers for this grade.

Preview all suppliers

Empfohlene Literatur

6061-T6 Aluminium – The Ultimate Guide

7075-T6 Aluminium: Overview & Properties

Aircraft Aluminium Grades

Cast vs. Wrought Aluminium: Standards, Properties and Applications

Precipitation Hardening (Age Hardening)

Alle anzeigen

Do you supply similar materials?

List your company on Matmatch now and reach engineers around the world looking for such materials.

Request more information

Eigenschaften

Allgemein

Property	Value	Condition	Related Standards
Dichte	2.72 g/cm³ Show Material materials with Dichte of 2.72 g/cm³	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547
	2.72 g/cm³ Show Material materials with Dichte of 2.72 g/cm³	H34
	2.8 g/cm³ Show Material materials with Dichte of 2.8 g/cm³	H34

Mechanisch

Property	Temperature	Value	Condition	Related Standards	Comment
Bending Fatigue Strength		105.0 MPa Show Material materials with Bending Fatigue Strength of 105.0 MPa	H34	AA Standards
Dauerfestigkeit		15 MPa Show Material materials with Dauerfestigkeit of 15 MPa	H34		for 5x10⁸ cycles
Dehnung	-195 °C	26 % Show Material materials with Dehnung of 26 %	H34		Elongation in 50 mm
	-80 °C	16 % Show Material materials with Dehnung of 16 %	H34		Elongation in 50 mm
		1.0 % Show Material materials with Dehnung of 1.0 %	H34	AA Standards, ASTM B209	A50
		2.0 % Show Material materials with Dehnung of 2.0 %	H34	AA Standards, ASTM B209	A50
		3.0 % Show Material materials with Dehnung of 3.0 %	H34	AA Standards, ASTM B209, ASTM B313	A50
		4.0 % Show Material materials with Dehnung of 4.0 %	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547	A50
		4.0 % Show Material materials with Dehnung of 4.0 %	H34	AA Standards, ASTM B209	A100
		5.0 % Show Material materials with Dehnung of 5.0 %	H34	AA Standards, ASTM B209, ASTM B547	A50
		7.1 % Show Material materials with Dehnung of 7.1 %	H34
		9.0 % Show Material materials with Dehnung of 9.0 %	H34	AA Standards	A50
		10.0 % Show Material materials with Dehnung of 10.0 %	H34	AA Standards	A100
	0 °C	13 % Show Material materials with Dehnung of 13 %	H34		Elongation in 50 mm
	24 °C	12 % Show Material materials with Dehnung of 12 %	H34		Elongation in 50 mm
	100 °C	13 % Show Material materials with Dehnung of 13 %	H34		Elongation in 50 mm
	150 °C	22 % Show Material materials with Dehnung of 22 %	H34		Elongation in 50 mm
	205 °C	35 % Show Material materials with Dehnung of 35 %	H34		Elongation in 50 mm
	260 °C	55 % Show Material materials with Dehnung of 55 %	H34		Elongation in 50 mm
	315 °C	80 % Show Material materials with Dehnung of 80 %	H34		Elongation in 50 mm
	370 °C	90 % Show Material materials with Dehnung of 90 %	H34		Elongation in 50 mm
Elastizitätsmodul		69.0 GPa Show Material materials with Elastizitätsmodul of 69.0 GPa	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547
		69 GPa Show Material materials with Elastizitätsmodul of 69 GPa	H34
Härte, Brinell		63.0 [-] Show Material materials with Härte, Brinell of 63.0 [-]	H34	AA Standards
		63.0 [-] Show Material materials with Härte, Brinell of 63.0 [-]	H34		500 kg load, 10 mm ball
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m			Typical for Wrought 3000 Series Aluminium
Poissonzahl		0.33 [-] Show Material materials with Poissonzahl of 0.33 [-]			Typical for Wrought 3000 Series Aluminium
Scherfestigkeit		125.0 MPa Show Material materials with Scherfestigkeit of 125.0 MPa	H34
Schubmodule		25.0 GPa Show Material materials with Schubmodule of 25.0 GPa	H34
Streckgrenze	-200 °C	235 MPa Show Material materials with Streckgrenze of 235 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02
	-100 °C	212 MPa Show Material materials with Streckgrenze of 212 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02
	-30 °C	200 MPa Show Material materials with Streckgrenze of 200 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02
		170.0 MPa Show Material materials with Streckgrenze of 170.0 MPa	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547	RP02
		200.0 MPa Show Material materials with Streckgrenze of 200.0 MPa	H34	AA Standards	RP02
		200.0 MPa Show Material materials with Streckgrenze of 200.0 MPa	H34
	25 °C	200 MPa Show Material materials with Streckgrenze of 200 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02
	100 °C	200 MPa Show Material materials with Streckgrenze of 200 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02
	200 °C	105 MPa Show Material materials with Streckgrenze of 105 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02
	300 °C	34 MPa Show Material materials with Streckgrenze of 34 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02
	400 °C	19 MPa Show Material materials with Streckgrenze of 19 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02
Zugfestigkeit	-195 °C	360 MPa Show Material materials with Zugfestigkeit of 360 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture
	-80 °C	262 MPa Show Material materials with Zugfestigkeit of 262 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture
		220.0 - 265.0 MPa Show Material materials with Zugfestigkeit of 220.0 - 265.0 MPa	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547
		240.0 MPa Show Material materials with Zugfestigkeit of 240.0 MPa	H34	AA Standards
	0 °C	248 MPa Show Material materials with Zugfestigkeit of 248 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture
	24 °C	240 MPa Show Material materials with Zugfestigkeit of 240 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture
	100 °C	235 MPa Show Material materials with Zugfestigkeit of 235 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture
	150 °C	193 MPa Show Material materials with Zugfestigkeit of 193 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture
	205 °C	145 MPa Show Material materials with Zugfestigkeit of 145 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture
	260 °C	97 MPa Show Material materials with Zugfestigkeit of 97 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture
	315 °C	52 MPa Show Material materials with Zugfestigkeit of 52 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture
	370 °C	35 MPa Show Material materials with Zugfestigkeit of 35 MPa	H34		up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

Thermisch

Property	Temperature	Value	Condition	Related Standards
Koeffizient der thermischen Ausdehnung		2.4e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.4e-05 1/K	H34
	20 °C	2.3899999999999998e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3899999999999998e-05 1/K	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547
	100 °C	2.3899999999999998e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3899999999999998e-05 1/K	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547
Schmelzpunkt		630.0 - 655.0 °C Show Material materials with Schmelzpunkt of 630.0 - 655.0 °C	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547
		630.0 °C Show Material materials with Schmelzpunkt of 630.0 °C	H34
Spezifische Wärmekapazität		890.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 890.0 J/(kg·K)	H34
Wärmeleitfähigkeit		160.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 160.0 W/(m·K)	H34
		163 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 163 W/(m·K)	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547

Elektrisch

Property	Value	Condition	Related Standards
Elektrische Leitfähigkeit	24000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 24000000.0 S/m	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547
spezifischer Widerstand	4.17e-08 Ω·m Show Material materials with spezifischer Widerstand of 4.17e-08 Ω·m	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547

Chemical properties

Property	Value	Condition	Related Standards
Aluminium	95.6 - 98.2 % Show Material materials with Aluminium of 95.6 - 98.2 %	H34
Andere	0.15 % Show Material materials with Andere of 0.15 %	H34
Eisen	0.70 % Show Material materials with Eisen of 0.70 %	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547
	0.7 % Show Material materials with Eisen of 0.7 %	H34
Kupfer	0.25 % Show Material materials with Kupfer of 0.25 %	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547
Magnesium	0.8 - 1.3 % Show Material materials with Magnesium of 0.8 - 1.3 %	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547
Mangan	1.0 - 1.5 % Show Material materials with Mangan of 1.0 - 1.5 %	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547
Silizium	0.3 % Show Material materials with Silizium of 0.3 %	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547
Zink	0.25 % Show Material materials with Zink of 0.25 %	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547

Technological properties

Property
Brazing	general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen
Corrosion properties	Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere
General machinability	General: poor (O, H32), sufficient (H34, H36, H38)
Workability	general (condition): good (O), acceptable (H32, H34), poor(H36, H38)

Looking for suppliers of this material? Click to see 23 supplier of AA Standards Grade 3004 H34 on Matmatch